影响HTV硅橡胶撕裂强度的因素  

Factors Affecting the Tear Strength of HTV Silicone Rubber

作　　者：韩庆文[1] 陈海平[1] 李恩[1] 梅平[1] 苗刚[1] 

机构地区：[1]湖北兴发化工集团股份有限公司,湖北宜昌443000

出　　处：《有机硅材料》2014年第3期172-175,共4页Silicone Material

摘　　要：考察了白炭黑种类、羟基硅油用量、含氢硅油用量以及不同乙烯基含量生胶并用对热硫化(HTV)硅橡胶撕裂强度的影响。结果显示,气相法白炭黑的补强效果强于沉淀法白炭黑,且比表面积越大,硅橡胶的撕裂强度越高;随着羟基硅油加入量的增加,硅橡胶的撕裂强度先增后趋于稳定;含氢硅油的用量对HTV硅橡胶的撕裂强度基本没有影响;高乙烯基含量生胶和低乙烯基含量生胶并用能显著提高HTV硅橡胶的撕裂强度。较佳配方是:166 g 110-0生胶,4 g 112生胶、80 g QS-102气相法白炭黑、8.5 g羟基硅油、1.0 g含氢硅油、0.5 g乙烯基硅油,此时,HTV硅橡胶的撕裂强度达到21 KN/m。The factors which affecting the tear strength of HTV silicone rubber , such as the types of fumed silica , content of the hydroxyl silicone oil and the hydrogenous silicone oil , and the combination of HTV silicone rubber gum with different vinyl contents , were discussed .Results show that fumed silica has a better reinforce-ment than the precipitated silica .The larger specific surface area is , the higher strength of HTV silicone rubber is.The tear strength of HTV silicone increases and keeps stable with the addition of hydroxyl silicone oil .The hydrogenous oil has no effect on the tear strength of HTV silicone rubber .The combination of the gum with high and low vinyl contents can significantly improve the tear strength of HTV silicone rubber .A preferred formula-tion is that 110-0 gum 166 g, 112 gum 4 g, QS-102 fumed silica 80 g, hydroxyl silicone oil 8.5 g, hydroge-nous silicone oil 1.0 g, vinyl silicone oil 0.5 g.The HTV silicone rubber shows a tear strength of 21 kN/m.

关 键 词：混炼 硅橡胶 撕裂强度 白炭黑 热硫化 乙烯基 羟基硅油 

分 类 号：TQ333.93[化学工程—橡胶工业]