Selective recovery of lead from zinc oxide dust with alkaline Na_2EDTA solution  

用碱性Na_2EDTA溶液从次氧化锌烟灰中选择性回收铅(英文)

作　　者：刘青[1] 杨声海[1] 陈永明[1] 何静[1] 薛浩天 

机构地区：[1]中南大学冶金与环境学院,长沙410083

出　　处：《Transactions of Nonferrous Metals Society of China》2014年第4期1179-1186,共8页中国有色金属学报（英文版）

基　　金：Project (50974138) supported by the National Natural Science Foundation of China;Project (2010ssxt158) supported by Graduate Student Innovation Foundation of Central South University,China

摘　　要：The selective recovery of lead from the zinc oxide dust using an alkaline Na2EDTA solution was investigated. The effects of temperature, leaching time, Na2EDTA concentration and initial NaOH concentration on the leaching rates of lead and zinc were studied. The following optimized leaching conditions were obtained： liquid-to-solid ratio 5：1 mL/g, stirring speed 650 r/min, Na2EDTA concentration 0.12 mol/L, initial NaOH concentration 0.5 mol/L, leaching temperature 70 ℃, leaching time 120 min. Under the optimized conditions, the average leaching rates of lead, zinc, fluoride and chloride are 89.92%, 0.94%, 62.84% and 90.02%, respectively. The filtrate was used to electrowin lead powders. The average current efficiency of electrowinning is about 93% and lead content is higher than 98% under the conditions of temperature of 60 ℃, current density of 200 A/m2, H3PO4 concentration of 1.5 g/L, and lead ion concentration of above 5 g/L. The consumption of Na2EDTA and the direct current are about respectively 0.218 kg and 0.958 kW·h for per kilogram of lead powder.采用碱性Na2EDTA溶液从次氧化锌烟灰中回收铅。探讨温度、浸出时间、Na2EDTA浓度和起始NaOH浓度对铅、锌浸出率的影响。得到最优实验条件如下:液固比5:1 mL/g、搅拌速度650 r/min、Na2EDTA浓度0.12mol/L、NaOH初始浓度0.5 mol/L、温度70°C、浸出时间120 min。在最优实验条件下,铅、锌、氟和氯的平均浸出率分别为89.92%、0.94%、62.84%和90.02%。浸出液用于电沉积铅粉。在温度为60°C、电流密度为200A/m2、H3PO4浓度为1.5 g/L、铅离子浓度不低于5 g/L时,电沉积铅粉平均电流效率大约为93%,阴极铅纯度高于98%。电沉积1 kg铅粉大约消耗0.218 kg Na2EDTA和0.958 kW·h电能。

关 键 词：LEAD zinc oxide dust alkaline Na2EDTA solution ELECTROWINNING LEACHING 

分 类 号：TF812[冶金工程—有色金属冶金]