磷石膏复分解法制备硫酸铵的研究  

Study of Production of Ammonium Sulfate through Metathesis Reaction of Phosphogypsum

作　　者：郑绍聪[1] 彭操[2] 王智娟[1] 朱丽萍[1] 贺池先[1] 

机构地区：[1]曲靖师范学院化学化工学院,云南曲靖655011 [2]云南省化工研究院,云南昆明650228

出　　处：《云南化工》2014年第3期1-4,共4页Yunnan Chemical Technology

基　　金：云南省高校煤资源开发利用及其污染控制重点实验室

摘　　要：以磷石膏和碳酸铵为原料,采用复分解法制备硫酸铵。考察了原料物质的量比、反应温度、反应时间、液固比、搅拌器转速等因素对磷石膏制备硫酸铵的影响。通过实验,确定了最佳工艺条件:原料液中CO2-3与SO2-4物质的量比为1.5,反应温度50℃,反应时间90 min,液固比为5.0,搅拌器转速为200 r/min以上。在此条件下,磷石膏制备硫酸铵转化率大于90.0%,产品质量分数大于98.0%。Using phosphogypsum as raw materials, ammonium sulfate through metathesis reaction was prepared. The influences of the raw ratio, reaction time, reaction temperature, feeding rate and liquid/solid ratio were studied. The results shown that the optimal operation parameters are as follows： the material ratio [n（CO3^2- ）/n（SO4^2- ） ] is 1.5, reaction temperature is 50℃, reaction time is 90 min, liquid/solid ratio is 5.0, agitator speed is above 200 r/min. Under the optimum process conditions, the average conversion rate from phosphogypsum is above 90.0%, and the product＇s purity is above 98.0%.

关 键 词：磷石膏 复分解法 硫酸铵 

分 类 号：TQ113.7[化学工程—无机化工]