石灰岩—水玻璃系统灌浆材料的研究  

作　　者：殷素红[1] 文梓芸[1] 

机构地区：[1]华南理工大学材料科学与工程学院,广州510640

出　　处：《新型建筑材料》2001年第1期42-45,共4页New Building Materials

基　　金：广东省自然科学基金项目!(960253);广州市建委科技项目!(98011)

摘　　要：首次探讨了石灰岩—水玻璃系统的胶凝反应。pH值测定证明该系统能反应 ,但反应较缓慢。从水玻璃角度研究了加速系统反应的影响因素 ,结果表明 :水玻璃中SiO2 处于某种过渡态 ,波美度大于45°,适当升高温度 ,均可加速系统反应。40℃养护下低品位石灰岩—水玻璃浆液小试体 (2cm×2cm×2cm)结石强度和固砂强度分别可达8 .3MPa和11.3MPa 。bstract:The cementing reaction of limestone-water glass system is probed into firstly.The measurement of PH value confirms that the system can react,but slowly. The impact factors of accelerating the system reaction are studied from angle of water glass. The result shows: SiO2 in water glass is at some transition status; Baume degree is bigger than 45°;to raise temperature properly may accelerate the system reaction. The cube(2cm x 2cm x 2cm)made of low purity limestone-water glass slurry cured at 40℃, with stone and sand binding powers of 8.3 MPa and 11.3 MPa respectively, may develop a new inorganic grouting material.

关 键 词：石灰岩 水玻璃 胶凝反应 灌浆材料 

分 类 号：TQ171.79[化学工程—玻璃工业]