核壳橡胶增韧环氧/玻璃纤维复合材料层压板性能的研究  

STUDY ON A GLASS WOVEN FABRIC PREPREG LAMINATE OF THE EPOXY MATRIX RESIN TOUGHENED WITH CORE-SHELL RUBBER PARTICLE

作　　者：李洪峰[1] 王德志[1] 曲春艳[1] 毛勇[1] 王海民[1] 

机构地区：[1]黑龙江省科学院石油化学研究院,哈尔滨150040

出　　处：《玻璃钢／复合材料》2014年第6期25-29,共5页Fiber Reinforced Plastics/Composites

基　　金：黑龙江省自然科学基金(ZD200907)

摘　　要：以核壳橡胶作为环氧树脂增韧剂,制备了一种高温固化环氧基体与玻璃纤维预浸料。结果表明,核壳橡胶用量为5phr时不影响环氧树脂对玻璃纤维的浸渍能力,此时核壳橡胶增韧后环氧/玻璃纤维层压板获得了较好的增韧效果,冲击强度达到278.1kJ/m2,比增韧前提高了20.0%;Ι型层间断裂韧性提高明显,达到982.0J/m2,比增韧前提高了35.4%;径向拉伸强度达到749.5MPa,比增韧前提高了16.5%,拉伸模量没有明显变化;SEM结果表明核壳橡胶增韧基体树脂的破坏断面为典型的韧性破坏,且树脂与玻璃纤维浸润性好、粘接力强。A glass woven fabric prepreg of the epoxy matrix resin toughened with core-shell rubber particles was prepared. The results showed that the core-shell rubber will not affect the epoxy resin infiltration capacity of glass fiber and fabric prepreg laminate achieved excellent toughness by using just 5phr core-shell rubber as tougher,impact strength of which reached 278. 1kJ /m^2and it increased by 20. 0% than that before toughening,fracture toughness GICof which reached 982. 0J /m^2and it increased by 35. 4% than before toughening; tensile strength of which reached 749. 5MPa and it increased by 16. 5% than that before toughening,tensile modulus of laminate toughened with core-shell rubber particle is hardly decreased,the surface morphology observed by scanning electron microscope exhibited typical toughness fracture. The resin has good infiltration and adhesion with glass fiber.

关 键 词：核壳橡胶 预浸料 复合材料力学性能 层压板Ⅰ型层间断裂韧性 

分 类 号：TB332[一般工业技术—材料科学与工程]