低腐蚀破胶剂的研究  

Study on Low Corrosion Gel Breaker

作　　者：陆原[1] 任奕[1] 王仲广[1] 逯学朝[1] 郭海军[1] 王铁钢[1] 

机构地区：[1]中海油能源发展股份有限公司工程技术分公司,天津300452

出　　处：《全面腐蚀控制》2014年第6期48-50,共3页Total Corrosion Control

摘　　要：针对氧化类的破胶剂引起的腐蚀问题,研究开发了一种复合型缓蚀剂BHH-DRH1,通过室内评价认为其很好地抑制了破胶剂JPC的腐蚀,推荐现场加注量为1.0%。该技术在南海某油田进行试用,取得了预期效果。An compound corrosion inhibitor BHH-DRH1 was developed in order to solve corrosion problem of oxidative gel breaker. It can be show that the inhibitor can decrease effectively corrosion of gel breaker JPC in laboratory test. It was suggested that the content of inhibitor was 1%. The technology was trialed in offshore oilfield, and the trial result reached expected effect.

关 键 词：氧化性 破胶剂 腐蚀 缓蚀剂 

分 类 号：TG174.42[金属学及工艺—金属表面处理]