粉煤灰基煤层压裂支撑剂的研究  

Study on Fly-ash Based Propping Agent for Coal Bed Fracturing

作　　者：高如琴[1] 吴洁琰 王紫括[2] 郝丹迪 

机构地区：[1]华北水利水电大学,郑州450011 [2]河南大学,开封475001

出　　处：《硅酸盐通报》2014年第6期1319-1322,共4页Bulletin of the Chinese Ceramic Society

基　　金：河南省教育厅自然科学研究计划项目(2011B610005)

摘　　要：采用粉煤灰为主要原料,铝矾土、高岭土、长石为烧结助剂,制备粉煤灰基支撑剂。结合TG-DTA、SEM、EDS、XRD等现代测试手段对样品的结构和性能进行了表征。结果表明:材料主要以O,A1,Si等元素为主,主晶相为莫来石和石英,晶粒之间有大量5～10μm的气孔。材料具有较好的圆球度,粒径为0.5～0.8 mm的煤层压裂陶粒支撑剂,体密度为0.998 g/cm^3,视密度为2.559 g/cm^3,酸溶解度为0.284%,22 MPa条件下,抗压破碎率为8.241%,导流能力67.24μm^2·cm。Using fly-ash as the main raw material, adding bauxite, kaolin and feldspar as sintering aids, fly-ash based propping agent was prepared. By the means of TG-DTA, XRD, SEM and other modern testing means, the structure and properties of the samples were characterized. The results show the propping agent with good sphericity, is mainly consist of O,Al, Si and other elements. The main crystal phase is mullite and quartz, there is a lot of 5-10 μm pores among the grains. The volume density, real density and acid solubility of propping agent for coal bed fracturing with particle size 0.5-0.8 mm are 0.998 g/cm3^ , 2. 559 g/cm^3 and 0. 284% respectively. In 22 MPa, the broken rate and flow conductivity are 8. 241% and 67.24 μm^2 . cm respectively.

关 键 词：粉煤灰 支撑剂 煤层压裂 结构和性能 

分 类 号：TQ174[化学工程—陶瓷工业]