Small-angle X-ray analysis of the effect of grain size on the thermal damage of octahydro-1, 3, 5, 7-tetranitro-1, 3, 5, 7 tetrazocine-based plastic-bounded expolsives  

作　　者：闫冠云 田强 刘佳辉 陈波 孙光爱 黄明 李秀宏 

机构地区：[1]Key Laboratory for Neutron Physics and Institute of Nuclear Physics and Chemistry,China Academy of Engineering Physics [2]Institute of Chemical Materials,China Academy of Engineering Physics [3]Institute of Shanghai Apply Physics,Chinese Academy of Sciences

出　　处：《Chinese Physics B》2014年第7期560-564,共5页中国物理B（英文版）

基　　金：supported by the National Natural Science Foundation of China(Grant Nos.11205137,11079043,and 11302199)

摘　　要：The microstmcture evolution of plastic-bonded explosives （PBXs） after thermal stimulus plays a key role in PBX performance. In this paper, the nanoscale pores of thermal-treated octahydro-1,3,5,7-tetranitro-1,3,5,7 tetrazocine （HMX）- based PBXs with different HMX particle sizes [approximately 40 （FLIP） and 100 μm （LHP）] were measured using small- angle X-ray scattering （SAXS）. No obvious pore variations were found in the LHP samples heated at 160 ℃ for 6 h, whereas the amount of pores of FHP decreased when subjected to 160 ℃ for 6 h. At 180 ℃, the average pore radii of FHP and LHP decreased from approximately 45 nm to 25 nm, and the total pore volume increased distinctively because of phase transformation. The LHP sample reached a high level of pore content after being held at 180 ℃ for 1 h, whereas FHP required 3 h. Both FHP and LHP had relatively high pore volumes when subjected to 200 ℃ for 1 and 3 h.The microstmcture evolution of plastic-bonded explosives （PBXs） after thermal stimulus plays a key role in PBX performance. In this paper, the nanoscale pores of thermal-treated octahydro-1,3,5,7-tetranitro-1,3,5,7 tetrazocine （HMX）- based PBXs with different HMX particle sizes [approximately 40 （FLIP） and 100 μm （LHP）] were measured using small- angle X-ray scattering （SAXS）. No obvious pore variations were found in the LHP samples heated at 160 ℃ for 6 h, whereas the amount of pores of FHP decreased when subjected to 160 ℃ for 6 h. At 180 ℃, the average pore radii of FHP and LHP decreased from approximately 45 nm to 25 nm, and the total pore volume increased distinctively because of phase transformation. The LHP sample reached a high level of pore content after being held at 180 ℃ for 1 h, whereas FHP required 3 h. Both FHP and LHP had relatively high pore volumes when subjected to 200 ℃ for 1 and 3 h.

关 键 词：HMX-based plastic-bonded explosives small-angle X-ray scattering pores thermal-treated 

分 类 号：O434.19[机械工程—光学工程]