再热裂纹新判据——(εr)min  

New criterion of reheat cracking——(ε_r)min

作　　者：罗志昌[1] 陈佩寅 张伟明[1] 秦瑞凯 

机构地区：[1]清华大学 [2]鞍山钢铁公司

出　　处：《焊接学报》1991年第3期136-142,共7页Transactions of The China Welding Institution

摘　　要：采用等温插销试验,铁研试验和高温拉伸试验对HQ80C钢的再热裂纹敏感性进行了详尽的研究。用ε_(?)>ε_(?)的应变概念探讨了再热裂纹的形成条件,提出示意图,该图较完整地解释了影响再热裂纹各因素之间的关系。文中提出再热裂纹的新判据——(εr)min,讨论了判据的合理性和优点。研究结果表明:(εr)min愈小,材料的再热裂纹敏感性愈大。The sensitivity of HQ80C steel to the reheat cracking was investigated by using the equi-temperature implant test, the Tekken test and the high-temperature tensile test. The conditions causing the reheat cracking were discussed utilizing the strain concept. Moreover, a scheme was proposed, which porfeotly discribes the relationship among the fectors affecting the reheat cracking. In this paper, the authors suggest a new oriterion of the reheat cracking——(ε_r)min, and desoribe its reasonableness and advantages. The less(ε_(?))min is, the higher is the sensi-tivity of the materials to reheat cracking.

关 键 词：再热裂纹 判据 低合金钢 高强度钢 

分 类 号：TG142.14[一般工业技术—材料科学与工程]