PMN和PZN基复相陶瓷的制备及其介电温度稳定性的研究  

The Fabrication and Dielectric-temperature Stability of Different Based Composite Ceramics

作　　者：杨祖培[1] 屈绍波[2] 崔斌[2] 高峰[2] 侯育冬[2] 田长生[2] 

机构地区：[1]陕西师范大学化学系,西安710062 [2]西北工业大学材料科学与工程学院,西安710072

出　　处：《材料工程》2001年第4期22-24,共3页Journal of Materials Engineering

基　　金：陕西省自然科学基金!资助项目 (2 0 0 0 C0 3)

摘　　要：以 PZN基和 PMN基粉体为起始组元 ,采用两相混合烧结法成功地制备了两相共存的复相陶瓷。介电性能测试结果表明 ,复相陶瓷的室温介电常数为 5 377(1k Hz) ,其介电温谱在 - 15℃～ + 90℃温度范围内相当平坦 ,介电温度稳定性大幅度提高。据键价理论讨论了复相陶瓷的设计和组成控制。并初步探讨了复相陶瓷提高介电温度稳定性的机制。By the method of mixed sintering, the composite ceramics consisting of two phases with PZN based and PMN based respectively were successfully prepared The experiments show that the composite ceramics exhibit high dielectric constant(5377) with flat temperature characteristic over a wide ranges of -15℃ to +90℃,which could be attributed to the separation of the low temperature phase (paraelectric phase) from the high temperature phase (polar microregions) in composite ceramics

关 键 词：复相陶瓷 PZN-BT PMN-PT 介电温度稳定性 铌镁酸铅 铌锌酸铅 制备 

分 类 号：TQ174.758[化学工程—陶瓷工业] TB332[化学工程—硅酸盐工业]