对含铬可锻铸铁件热处理技术的探讨  

An Approach on the Heat Treatment Technique of Malleable Cast Iron Containing Chromium

作　　者：王素洁[1] 梁文心[1] 杨殿魁[1] 李进富[1] 

机构地区：[1]内蒙古工业大学,呼和浩特市010062

出　　处：《现代铸铁》2001年第1期45-47,共3页Modern Cast Iron

摘　　要：对含铬的可锻铸铁进行了石墨化退火试验，试验证明，当含铬量为 0.09％时，不可能得到铁素体基体，而用低温波动式保温退火工艺，得到了粒状珠光体＋团絮状石墨组织，其σ b大于 300MPa，δ大于 6％，机械加工性能良好，这不失为一种挽救含铬高的可锻铸铁件的可行工艺。An experiment on graphitizing annealing of malleable cast iron containing chromium was carried out.The results showed that ferrite could not be obtained with the chromium content of 0.09％ ,however,a low temperature annealing process with waving type of temperature holding resulted in the structure of granular pearlite plus tempered graphite and the tensile strength was more than 300MPa,the elongation was more than 6％ .It’ s indeed a practical annealing process for rescuing the malleable cast iron with high chromium content.

关 键 词：波动式石墨化退火 粒状珠光体 可锻铸铁件 热处理 铬 

分 类 号：TG164.4[金属学及工艺—热处理]