Phase Transitions and Structures of Poly(ethylene-co-chlorotrifluoroethylene)  

作　　者：J.M.DEITZEL Bojie WANG Ping HUANG L.Lawrence CHAPOY Stephen Z.D.CHENG 

机构地区：[1]The Maurice Morton Institute and Department of Polymer Science,The University of Akron,Akron Ohio 44325-3909,U.S.A.

出　　处：《应用化学》2001年第5期301-309,共9页Chinese Journal of Applied Chemistry

摘　　要：Poly(ethylene- co -chlorotrifluoroethylene) with a 1∶1 molar ratio of ethylene and chlorotrifluoroethylene in composition, PECTFE, is a statistically alternating copolymer widely used in cable coating industry. PECTFE has been commonly characterized as a semicrystalline polymer with crystals melting at 238 ℃. Differential scanning calorimetry, thermal mechanical analysis and dynamic mechanical analysis indicated that PECTFE undergoes a reversible solid-solid transition during cooling and heating in the temperature range between 100 ℃ and 200 ℃. Based on detailed structural analysis via wide angle X-ray diffraction and electron diffraction techniques, we proposed that PECTFE possesses a hexagonal phase above 200 ℃( a =0 60 nm, c =0 49 nm) and an orthorhombic phase( a =0 99 nm, b =0 57 nm, c =0 49 nm) at room temperature.Poly(ethylene- co -chlorotrifluoroethylene) with a 1∶1 molar ratio of ethylene and chlorotrifluoroethylene in composition, PECTFE, is a statistically alternating copolymer widely used in cable coating industry. PECTFE has been commonly characterized as a semicrystalline polymer with crystals melting at 238 ℃. Differential scanning calorimetry, thermal mechanical analysis and dynamic mechanical analysis indicated that PECTFE undergoes a reversible solid-solid transition during cooling and heating in the temperature range between 100 ℃ and 200 ℃. Based on detailed structural analysis via wide angle X-ray diffraction and electron diffraction techniques, we proposed that PECTFE possesses a hexagonal phase above 200 ℃( a =0 60 nm, c =0 49 nm) and an orthorhombic phase( a =0 99 nm, b =0 57 nm, c =0 49 nm) at room temperature.

关 键 词：乙烯 1-氯-3氟乙烯 共聚物 结构 

分 类 号：O632.11[理学—高分子化学]