低温烧结用PZT粉体水热合成  

AYNTHESIS OF PZT POWDER FOR LOW-TEMPERATURE SINTERING BY HYDROTHERMALLY METHOD

作　　者：胡志强[1] 奥谷昌之[2] 金子正治[2] 

机构地区：[1]大连轻工学院材料系,大连116034 [2]静冈大学工学部物资工学科

出　　处：《中国陶瓷》2001年第2期7-10,共4页China Ceramics

基　　金：国家教育部留学基金资助

摘　　要：水热合成了低温烧结用PZT粉体。合成时添加Fe+ 2 ,Bi+ 3 ,Cu+ 2 等离子化合物 ,生成粉体中外加微量Ba(Cu0 .5W0 .5)O3 ,经X -ray,SEM ,TG -DTA及比表面积的测定 ,表明当反应介质为 4mol/LNaOH ,时间 2h,反应温度 2 0 0°C时 ,合成的粉体中PZT微晶子已大量生成。PZT陶瓷在 850°C温度下烧成 ,密度可达理论值 98%。并对其压电性能进行了测定 ,结果证实 ,微量烧结助剂的添加除有效地降低烧结温度外 ,使Qm 值提高 ,而Kp值有所下降。。PZT powder for low-temperature sintering is synthesized by hydrothermally method,and,its electrical properies are measured.PZT powder is characterized by X-ray,SEM,TG-TGA,and specific surface area.It is found that addition of some inorganic compounds containing Fe +2,Bi +3,or Cu +2 benefits formation of PZT ceramics. PZT ceramics is sintered with trace of BCW and PZT powder obtained in 4M sodium hydroxide solution at 200℃ for 2 hours,in which PZT micro crystal is found.The density of obtained PZT ceramics is 98 percentage of the theoretical value.As well as,adding trace of sintering additives can increase the Qm value,whereas decrease the Kp value of PZT ceramics.

关 键 词：水热合成 低温烧结 PZT粉末 锆钛酸铅 

分 类 号：TQ174.758[化学工程—陶瓷工业] TQ134.53[化学工程—硅酸盐工业]