TiAl基合金的氧化分层  

Oxidation stratification of TiAl based alloy

作　　者：曲恒磊[1] 周廉[1] 魏海荣[1] 赵永庆[1] 

机构地区：[1]西北有色金属研究院,西安710016

出　　处：《中国有色金属学报》2001年第3期398-403,共6页The Chinese Journal of Nonferrous Metals

摘　　要：用SEM及EDS研究了 5种TiAl基合金经 80 0～ 10 0 0℃ ,10 0h断续氧化及循环氧化后氧化剖面的结构、组成。结果显示 ,TiAl氧化表面存在分层现象。首先形成 (TiO2 +Al2 O3 )混合层 ,其次是新相过渡层 ;较少观察到连续的Al2 O3 层。因应力作用 ,氧化层开裂乃至剥离后 ,化学分层转入物理分层阶段 ,氧化层保护性恶化。Interrupted or cyclic oxidation of five TiAl based alloys at 800～1?000?℃,100?h were carried out, cross section microstructure and oxides constitution were investigated by SEM, EDS equipments. The results show that stratification is one of the characteristics of oxidation of TiAl. Mixture layer of TiO 2+Al 2O 3 is formed firstly, after that there is the formation of diffusion zone inside and pure TiO 2 scale outside. Continuous Al 2O 3 film is observed scarcel. Chemical stratification is transformed into physical stratification once delamination occurs due to the effect of growth stress and thermal stress, and the protection of oxide layers is destroyed consequently. [

关 键 词：氧化 分层 生长应力 热应力 金属间化合物 TIAL合金 

分 类 号：TG172.82[金属学及工艺—金属表面处理] TG146.2[金属学及工艺—金属学]