TiC_P/H13(4Cr5MoV1Si)复合材料的显微组织和力学性能  

Microstructure and mechanical properties of TiC_P/H13 (4Cr5MoV1Si) composites

作　　者：孙建荣[1] 孙扬善[1] 樊泉[1] 

机构地区：[1]东南大学材料科学与工程系,南京210096

出　　处：《材料科学与工艺》2001年第2期146-149,共4页Materials Science and Technology

摘　　要：用熔铸工艺过程中的原位反应合成方法制备了含 φ(TiC)为 5 %颗粒增强的H13钢基复合材料 .实验结果表明 ,用本文工艺制备的复合材料工艺性能优良 ,易于加工成形 .显微组织中TiC颗粒分布均匀 ,没有出现颗粒的团聚及由于TiCP颗粒引入而形成的组织缺陷 .TiC颗粒的加入能有效地提高材料的常温、高温强度和耐磨性能 。In the present investigation TiC P/H13 steel composites with 5vol%TiC P were prepared by in situ reaction during melting processing. Experimental results show that the composites have good workability and machinability. The distribution of TiC particles in the microstructure is quite uniform and no apparent particle segregation and microdefects are observed. The addition of TiC particles results in a significant increase in strength at normal and elevated temperatures and wear resistance, but a decrease in ductility and toughness.

关 键 词：复合材料 力学性能 原位反应 显微组织 H13钢 碳化钛颗粒增强 