不同硅铝比的Cu-ZSM-5/堇青石整体式催化剂的NO分解反应性能  

NO Decomposition on Cu-ZSM-5/Cordierite Monolithic Catalyst Samples with Different Si/Al Ratios

作　　者：单学蕾[1] 关乃佳[1] 曾翔[1] 陈继新[1] 项寿鹤[1] Ursula ILLGEN Manfred BAERNS 

机构地区：[1]南开大学化学学院新催化材料科学研究所,天津300071 [2]柏林应用化学研究所

出　　处：《催化学报》2001年第3期242-244,共3页

摘　　要：考察了原位合成的不同硅铝比的Cu ZSM 5 /堇青石整体式催化剂上的NO分解反应 .结果表明 ,在 5 73～773K的温度范围内 ,硅铝比分别为 6 0 ,5 5和 40的催化剂在 72 3K下NO的转化率最高 ,而硅铝比小于 2 5的催化剂上的NO转化率很低 .低温有利于N2 O的生成 .整体式催化剂上的NO转化率低于单纯的分子筛催化剂Cu ZSM 5 。The NO decomposition reaction on Cu ZSM 5/cordierite monolithic catalyst samples with different Si/Al ratios was carried out at 723 K and GHSV=10?000 h -1 with NO ( ω =2×10 -3 ) in He. The results indicated that a higher Si/Al ratio favors the conversion of NO. Little amount of N 2O was found in the products when the reaction temperature was over 623 K. The turnover frequency (TOF) for NO decomposition on the Cu ZSM 5/cordierite monolithic catalyst was higher than that on the pure Cu ZSM 5 zeolite catalyst.

关 键 词：铜 ZSM-5分子筛 堇青石 整体式催化剂 一氧化氮 分解 反应性能 转化率 

分 类 号：O643.3[理学—物理化学]