铝合金表面覆盖SiO_2直接氧化生长的反应机理  

Interaction Mechanism of Molten Aluminium-Alloy and SiO_2 Surface Dopant in Directed Oxidation

作　　者：袁森[1] 都业志[1] 王武孝[1] 

机构地区：[1]西安理工大学材料科学与工程学院,西安710048

出　　处：《材料导报》2001年第6期58-60,共3页Materials Reports

基　　金：陕西省自然科学研究计划项目(98C14)

摘　　要：通过热力学计算和XRD分析,确定了Al-Mg-Si合金熔体与SiO_2表面覆盖剂反应的生成物相为Al_2O_3、Al、Si和MgAl_2O_4。直接金属氧化动力学实验表明,SiO_2 与熔体的接触反应加快了初期的传质过程,使微观传输通道始终处于活性状态,生成的 Al_2O_3 构筑了材料的初始骨架,Al_2O_3/Al 复合材料氧化生长的孕育期消失。In this paper,the phase structure of the interaction products of molten aluminium alloy with SiO_2 surface dopant during the Al_2O_3/Al composite growth is determined by means of thermodynamical calculation and X- ray diffraction analysis.The directed metal oxidation kinetic test results show that inoculation period of Al_2O_3/Al composite growth may disappear.The contact reaction of SiO_2 and molten aluminium alloy leads to the incipient mass diffusion transmission speeding up and the microcosmic transmission passageway becoming active.The resulting Al_2O_3 provides initial framework of Al_2O_3/Al composites.

关 键 词：直接金属 复合材料 表面覆盖剂 反应机理 直接氧化生长 铝合金 二氧化硅 陶瓷 金属 

分 类 号：TB333[一般工业技术—材料科学与工程]