多孔La_(1-x)Sr_xMnO_3的制备及表征  

Preparation and characterization of porous La_(1-x)Sr_xMnO_3

作　　者：夏长荣[1] 许大刚[1] 高建峰[1] 孟广耀[1] 彭定坤[1] 

机构地区：[1]中国科学技术大学材料科学与工程系,安徽合肥230026

出　　处：《功能材料》2001年第3期269-271,共3页Journal of Functional Materials

基　　金：国家自然科学基金资助项目(29801003;29631020)

摘　　要：用固相烧结法研制固体氧化物燃料电池的多孔阴极支撑体Ｌａ０．８Ｓｒ０．２ＭｎＯ３（ＬＳＭ）。实验研究了ＬＳＭ径向收缩率、孔隙率、孔径大小等多孔陶瓷的特征量与烧结温度、有机添加剂量等制备条件的关系。用扫描电子显微镜分析了ＬＳＭ的烧结性能，同时用四端子法研究了多孔ＬＳＭ的电导率、电导活化能等与 ＬＳＭ 孔隙率的关系。Porous La1-xSrSrxMnO3 (LSM) which could be used as cathode in solid state oxide fuel cells was prepared by solid state reaction of La2O3, SrCO3 and MnCO3. Shrinkage, porosity and pore size of the porous LSM were investigated as a function of sintering temperature and amount of organic additives. It was found that pore size as well as porosity was dependent on sintering temperature and amount of organic additives. However, shrinkage was affected only by sintering temperature. Electronic conductivity of the porous LSM was studied by four-probe method. Results show that activation energy for electronic conduction decreases with porosity. By fitting conductivity data with σ=σ0 (1-P)x, σ0 and x were 161 S/cm and 1.5, respectively at 850°C.

关 键 词：混合导体 多孔陶瓷 燃料电池 锰酸锶镧 制备 表征 

分 类 号：TM911.4[电气工程—电力电子与电力传动] TG174.754[金属学及工艺—金属表面处理]