β-NiOOH的研究(Ⅱ)电极充放电反应机理  

Studies on β-NiOOH (Ⅱ) Reaction mechanism of charge/discharge

作　　者：夏熙[1] 潘仁[1] 郭再萍[1] 

机构地区：[1]新疆大学应用化学研究所,新疆乌鲁木齐830046

出　　处：《电源技术》2001年第3期203-205,共3页Chinese Journal of Power Sources

摘　　要：以 β Ni(OH) 2 为原料采用温和化学氧化法合成 β NiOOH ,利用交流阻抗技术、恒电位阶跃技术和循环伏安技术对合成产物的电极反应机理进行了研究 ,认为 β NiOOH还原过程中含有一吸附过程 ,而 β Ni(OH) 2 氧化过程中不含有吸附过程 ,且反应 β NiOOHβ Ni(OH ) 2 为一准可逆反应过程。利用恒电位阶跃技术测定了模拟电极的质子扩散系数 ,充电态 β NiOOH中质子扩散系数为 3 .2× 10 -9cm2 ·s-1,而放电态 β Ni(OH ) 2 中质子扩散系数为 1.4× 10 -12cm2 ·s-1。NiOOH was prepared by chemical oxidation method with β-Ni(OH) 2 as raw material. The reaction mechanism of the product was studied by AC impendance technique and cyclic voltammetry technique (CV). The results show that the reduction of β-NiOOH includes an absorption process while the oxidation of β-Ni(OH) 2 does not include it. The reaction of β-NiOOH β-Ni(OH) 2 is a quasi-reversible process. The diffusion coefficients of protons (D) in the analogue electrode were measured by potentiastat-step technique (D β-NiOOH = 3.2×10 -9 cm 2·s -1 , D β-Ni(OH) 2 =1.4×10 -12 cm 2·s -1 ).

关 键 词：电池 镍电极 Β-NIOOH 放电 充电 

分 类 号：TM911[电气工程—电力电子与电力传动]