悬浮铸造工艺对EPC铸造低铬白口铸铁性能的影响  

Effect of Suspension Casting on the Property of Low-Chromium White Cast Iron Produced by the EPC Process

作　　者：刘根生[1] 王文才[1] 张志明[1] 刘金海[1] 李丘林[1] 

机构地区：[1]河北工业大学材料科学与工程学院,天津300130

出　　处：《铸造》2001年第11期666-669,共4页Foundry

摘　　要：针对常规EPC铸造生产低铬白口铸铁时综合性能较差的问题 ,采用悬浮铸造工艺将悬浮剂置于EPS模中 ,充型过程中悬浮剂均匀分布于铸型中 ,可改变金属液的结晶凝固特性 ,细化铸铁组织 ,并使部分微区内碳化物的类型发生质的变化 ,结果使低铬白口铸铁的综合性能得以显著提高。与常规方法相比 ,低铬白口铸铁的冲击韧性提高了2 4 5 % ,硬度提高了HRC4～HRC4 5 ,相对耐磨性提高了 35 %。Aiming at the problem of low chromium white cast iron produced by the EPC process with bad synthetic mechanical property, we adopt the suspending casting method by filling a suspending agent in EPS, so make the solidification characters of liquid metal changed, the microstructure of the iron refined and the type of carbide in some micro areas changed during solidification process, thus make the synthetic mechanical property of low chromium white cast iron produced by EPC process significantly increased. Compared with one produced by common EPC process, its impact toughness is improved by 24 5%, hardness strengthened by HRC4～HRC4 5, wear resistance raised by 35%.

关 键 词：悬浮铸造 悬浮剂 低铬白口铸铁 力学性能 负压实型铸造 

分 类 号：TG252[金属学及工艺—铸造]