TiC颗粒增强2618复合材料的研究  

Study on the TiC patricle strengthening 2618 composite

作　　者：龙春光[1] 伍先明[1] 魏晓娟[2] 

机构地区：[1]湘潭工学院机械工程系,湖南湘潭411201 [2]湘潭工学院土木工程系,湖南湘潭411201

出　　处：《湘潭矿业学院学报》2001年第4期32-35,共4页Journal of Xiangtan Mining Institute

摘　　要：用原位反应合成法 (即XD法 )制备了TiC颗粒增强 2 618复合材料 ,并用X -ray衍射分析技术、透射电镜及拉伸实验对其结构和性能进行了研究 结果表明 :利用原位反应合成法可以制备TiC增强多元素合金 2 618为基体的复合材料 ;与普通熔铸法相比 ,逆向熔铸法可以缩短熔铸时间 ,减少TiC粒子损失 ,从而制得较为理想的复合材料 ;TiC粒子的加入可以提高 2 618合金的力学性能 图 6,表 1,参The TiC particle strengthened 2618 composite was prepared by the in-situ synthesized method(or XD method). The constituent and properties of the composite have been investigated by the X-ray diffraction ,TEM technique and tensile experiment . Results show that: It is possible to prepare TiC particle strengthening multiple alloy 2618 matrix composite by XD method; To compare with the common melting and casting method, the reverse melting and casting method can shorten the melting time and effectively reduce the loss of TiC and get the ideal composite; With the addition of TiC particles, the mechanical properties of the 2618 alloy can be enhanced.6figs.,1tab.,8refs.

关 键 词：TIC颗粒 2618复合材料 原位反应合成法 碳化钛颗粒 XD法 

分 类 号：TB33[一般工业技术—材料科学与工程]