Ti-IF钢第二相粒子在热轧过程中析出行为的热模拟研究  被引量:3

STUDY ON PRECIPITATION BEHAVIOR OF TI-IF STEEL DURING HOT ROLLING THROUGH THERMO-MECHANICAL SIMULATION

在线阅读下载全文

作  者:商建辉[1] 王先进[1] 蒋冬梅[1] 孔冰玉[2] 陆匠心[2] 

机构地区:[1]北京科技大学 [2]上海宝钢集团公司

出  处:《钢铁》2002年第1期56-60,共5页Iron and Steel

基  金:国家"九五"攻关资助项目 ( 95 -5 2 7-0 1-0 1-0 1-0 7-1)

摘  要:对 Ti- IF钢进行再加热、热轧及卷取等过程的热模拟试验 ,用透射电镜对样品中析出物的形貌进行了观察 ,系统研究了各析出物在热轧过程中变化的全过程。结果表明 ,Ti N粒子在热轧和卷取过程中变化不大、比较稳定 ;Ti S和 Ti4C2 S2 粒子在热轧过程中继续析出、长大 ,并发生 Ti S与 Ti4C2 S2 的转变 ;Ti C粒子主要在热轧和卷取过程中析出。Thermo mechanical simulation test was carried out to simulate the process of reheating, hot rolling and coiling of Ti IF steel, the precipitation behavior of precipitates was observed and analyzed by transmission electron microscope (TEM) during the hot rolling. It is shown that TiN particles are stabile during the hot rolling and coiling, TiS and Ti 4C 2S 2 particles continue to precipitate and coarse during the hot rolling, and TiS changes to Ti 4C 2S 2, TiC particles mainly precipitate and coarsen during the hot rolling and coiling.

关 键 词:TI-IF钢 析出 热模拟 热轧 再热 卷取 

分 类 号:TG335[金属学及工艺—金属压力加工]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象