Some paradoxical observations about spheroidal graphite degeneracy  

作　　者：Jacques Lacaze Jon Sertucha 

机构地区：[1]CIRIMAT,Université de Toulouse,BP 44362,F-31030Toulouse,France [2]Investigaeiòn y Desarrollo de Procesos Metalúrgicos,IK4-Azterlan,Aliendalde auzunea 6,E-48200Durango(Bizkaia),Spain

出　　处：《China Foundry》2018年第6期457-463,共7页中国铸造（英文版）

摘　　要：Differential thermal analysis experiments have been performed on samples machined from Y2-blocks cast with different high-silicon spheroidal graphite irons. Depending on magnesium, silicon, cerium and antimony content, the as-cast microstructure showed various levels of chunky graphite in the central part of the blocks. In contrast, the microstructure of the materials after remelting and resolidification during differential thermal analysis consisted of lamellar or compacted graphite. The formation of chunky graphite in the as-cast microstructure is rationalized using an index or silicon equivalent that has been recently suggested. The differences in the microstructures after differential thermal analysis are discussed in terms of available free magnesium. Emphasis is finally put on the striking differences in characteristic size of the microstructures made of compacted graphite as compared to lamellar graphite and chunky graphite. This leads to tentative conclusions about growth of compacted and chunky graphite which would be worthy of further experimental investigations.Differential thermal analysis experiments have been performed on samples machined from Y2-blocks cast with different high-silicon spheroidal graphite irons. Depending on magnesium, silicon, cerium and antimony content, the as-cast microstructure showed various levels of chunky graphite in the central part of the blocks. In contrast, the microstructure of the materials after remelting and resolidification during differential thermal analysis consisted of lamellar or compacted graphite. The formation of chunky graphite in the as-cast microstructure is rationalized using an index or silicon equivalent that has been recently suggested. The differences in the microstructures after differential thermal analysis are discussed in terms of available free magnesium. Emphasis is finally put on the striking differences in characteristic size of the microstructures made of compacted graphite as compared to lamellar graphite and chunky graphite. This leads to tentative conclusions about growth of compacted and chunky graphite which would be worthy of further experimental investigations.

关 键 词：high-silicon SPHEROIDAL GRAPHITE iron GRAPHITE DEGENERACY COMPACTED GRAPHITE chunky GRAPHITE 

分 类 号：TG143.5[一般工业技术—材料科学与工程]