Highly selective catalytic reduction of NO_x by MnO_x–CeO_2–Al_2O_3 catalysts prepared by self-propagating high-temperature synthesis  

作　　者：Chao Wang Feng Yu Mingyuan Zhu Changjin Tang Ke Zhang Dan Zhao Lin Dong Bin Dai 

机构地区：[1]Key Laboratory for Green Processing of Chemical Engineering of Xinjiang Bingtuan, School of Chemistry and Chemical Engineering,Shihezi University [2]Key Laboratory of Mesoscopic Chemistry of Ministry of Education, School of Chemistry and Chemical Engineering, Nanjing University

出　　处：《Journal of Environmental Sciences》2019年第1期124-135,共12页环境科学学报（英文版）

基　　金：supported by the National High Technology Research and Development Program of China (863 program) (No.2015AA03A401);the Program for Changjiang Scholars and Innovative Research Team in University (No.IRT_15R46);the program of Science and Technology Innovation Team in Bingtuan (No.2015BD003)

摘　　要：We first present preparation of MnOx–CeO_2–Al_2O_3 catalysts with varying Mn contents through a self-propagating high-temperature synthesis(SHS) method, and studied the application of these catalysts to the selective catalytic reduction of NOxwith NH3(NH_3-SCR).Using the catalyst with 18 wt.% Mn(18 MnCe1Al2), 100% NO conversion was achieved at 200°C and a gas hourly space velocity of 15384 hr-1, and the high-efficiency SCR temperature window, where NO conversion is greater than 90%, was widened to a temperature range of 150–300°C. 18 MnCe1Al2 showed great resistance to SO_2(100 ppm)and H_2O(5%) at 200°C. The catalysts were characterized using X-ray diffraction, X-ray photoelectron spectroscopy, Brunauer–Emmett–Teller(BET) analysis, scanning electron microscopy, Fourier transform infrared spectroscopy, and H_2 temperature programmed reduction. The characterization results showed that the surface atomic concentration of Mn increased with increasing Mn content, which led to synergism between Mn and Ce and improved the activity in the SCR reaction. 18 MnCe1Al2 has an extensive pore structure,with a BET surface area of approximately 135.4 m^2/g, a pore volume of approximately 0.16 cm^3/g, and an average pore diameter of approximately 4.6 nm. The SCR reaction on 18 MnCe1Al2 mainly followed the Eley-Rideal mechanism. The performances of the MnOx–CeO_2–Al_2O_3 catalysts were good, and because of the simplicity of the preparation process,the SHS method is applicable to their industrial-scale manufacture.We first present preparation of MnOx–CeO_2–Al_2O_3 catalysts with varying Mn contents through a self-propagating high-temperature synthesis(SHS) method, and studied the application of these catalysts to the selective catalytic reduction of NOxwith NH3(NH_3-SCR).Using the catalyst with 18 wt.% Mn(18 MnCe1Al2), 100% NO conversion was achieved at 200°C and a gas hourly space velocity of 15384 hr-1, and the high-efficiency SCR temperature window, where NO conversion is greater than 90%, was widened to a temperature range of 150–300°C. 18 MnCe1Al2 showed great resistance to SO_2(100 ppm)and H_2O(5%) at 200°C. The catalysts were characterized using X-ray diffraction, X-ray photoelectron spectroscopy, Brunauer–Emmett–Teller(BET) analysis, scanning electron microscopy, Fourier transform infrared spectroscopy, and H_2 temperature programmed reduction. The characterization results showed that the surface atomic concentration of Mn increased with increasing Mn content, which led to synergism between Mn and Ce and improved the activity in the SCR reaction. 18 MnCe1Al2 has an extensive pore structure,with a BET surface area of approximately 135.4 m^2/g, a pore volume of approximately 0.16 cm^3/g, and an average pore diameter of approximately 4.6 nm. The SCR reaction on 18 MnCe1Al2 mainly followed the Eley-Rideal mechanism. The performances of the MnOx–CeO_2–Al_2O_3 catalysts were good, and because of the simplicity of the preparation process,the SHS method is applicable to their industrial-scale manufacture.

关 键 词：NH3-SCR SHS method MnOx-CeO2-Al2O3 CATALYST NOx REMOVAL efficiency 

分 类 号：X[环境科学与工程]