极高密度ITO坯体的制备和低温、欠氧烧结研究  

Preparation of High-density ITO Green Body

作　　者：杨硕[1] 薛建强[1] 师琳璞[1] YANG Shuo;XUE Jianqiang;Sill Linpu(Luoyang Ship Material Research Institute,Luoyang 471023,China)

机构地区：[1]中国船舶重工集团公司第七二五研究所,河南洛阳471023

出　　处：《材料开发与应用》2018年第6期68-73,共6页Development and Application of Materials

基　　金：国家战略性新兴产业发展专项(发改办高技[2012]1029号)

摘　　要：以平均粒径为50 nm的气化ITO粉体为原料,加入占原料1. 2%的分散剂聚碳酸酯,经球磨、陈腐后再"二次球磨"得到高固含量浆料,而后采用加压注浆成型获得了极高密度坯体。研究了浆料固相含量和粘度的关系,同时研究了浆料固相含量、陈腐时间与坯体密度的关系。将不同密度坯体在较低温度1 530℃和空气(欠氧)气氛中进行烧结,研究了坯体密度对靶材密度的影响规律。结果表明,在1 530℃、欠氧气氛烧结条件下,极高密度ITO坯体(相对密度75%)烧结后可得到外观黑色、相对密度为98. 3%的靶材,其密度远高于其他密度更低坯体所烧结的靶材。High solid content slurry was prepared by ball-milling and staleness and then by secondary ball-milling with arc evaporated ITO powdes with average grain-size of 50 nm added 1. 2% polycarbonate dispersant. Then high-density green body was prepared by stress-casting and the relationship betweem solid content and viscosities was studied,so was the relationship between green-body’s density and solid content in connection with staling time of slurry. The relation of density of green body and target was spotlighted by different density green-bodies sintered at 1 530 ℃ in low-oxygen air atmosphere. The result showed that the target of 98. 3% relative density whose superficial color was black was capable of being prepared by sintering the ITO green body whose relative density was 75% in 1 530 ℃ in low-oxygen air atmosphere,which demonstrated that the density of this black target was much higher than those of other ones from green-bodies of lower densities.

关 键 词：气化ITO粉 陈腐 二次球磨 极高密度坯体 

分 类 号：TF124[冶金工程—粉末冶金]