Sulfur-resistant methanation over MoO_3/CeO_2–ZrO_2 catalyst: Influence of Ce-addition methods  

作　　者：Zhaopeng Liu Yan Xu Zhenhua Li Baowei Wang Weihan Wang Xinbin Ma Renjie Liu 

机构地区：[1]Key Laboratory for Green Chemical Technology of Ministry of Education, School of Chemical Engineering and Technology, Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), Tianjin University

出　　处：《Journal of Energy Chemistry》2019年第1期31-38,共8页能源化学（英文版）

基　　金：Financial supports from the National High Technology Research and Development Program of China (863 Project) (2015AA050504);the National Natural Science Foundation of China (21576203)

摘　　要：In this paper, Ce_(0.2)Zr_(0.8)O_2 composite supports were prepared by different Ce-addition methods including impregnation of cerium(CeZr-imp), impregnation of citric acid and cerium(CeZr-CA) simultaneously and deposition precipitation method(CeZr-DP), respectively. The as-prepared supports were applied to prepare 10 wt% MoO_3/Ce_(0.2)Zr_(0.8)O_2 catalysts for sulfur-resistant methanation. The N_2 adsorption/desorption,X-ray diffraction(XRD), Raman spectroscopy(RS), X-ray photoelectron(XPS), temperature-programmed reduction by hydrogen(H_2-TPR) were undertaken to get textural properties, morphological information and structures of the catalysts. The results showed that Mo O_3 was highly dispersed on the surface of these three supports and Ce was mostly of coexisted in Ce^(4+)/Ce^(3+) redox pairs. Compared with Mo/CeZrimp, the CO conversion increased by 10% and 15% for Mo/CeZr-CA and Mo/CeZr-DP, respectively. This was mainly attributed to the larger specific surface area, Ce^(3+) concentration and content of active MoS_2 on the surface of catalysts.In this paper, Ce_(0.2)Zr_(0.8)O_2 composite supports were prepared by different Ce-addition methods including impregnation of cerium(CeZr-imp), impregnation of citric acid and cerium(CeZr-CA) simultaneously and deposition precipitation method(CeZr-DP), respectively. The as-prepared supports were applied to prepare 10 wt% MoO_3/Ce_(0.2)Zr_(0.8)O_2 catalysts for sulfur-resistant methanation. The N_2 adsorption/desorption,X-ray diffraction(XRD), Raman spectroscopy(RS), X-ray photoelectron(XPS), temperature-programmed reduction by hydrogen(H_2-TPR) were undertaken to get textural properties, morphological information and structures of the catalysts. The results showed that Mo O_3 was highly dispersed on the surface of these three supports and Ce was mostly of coexisted in Ce^(4+)/Ce^(3+) redox pairs. Compared with Mo/CeZrimp, the CO conversion increased by 10% and 15% for Mo/CeZr-CA and Mo/CeZr-DP, respectively. This was mainly attributed to the larger specific surface area, Ce^(3+) concentration and content of active MoS_2 on the surface of catalysts.

关 键 词：Sulfur-resistant METHANATION Ce introducing METHODS REDUCIBLE CE^3+ Synthetic natural gas Active MoS2 