Effect of poly(ethylene glycol) molecular weight on CO_2/N_2 separation performance of poly(amide-12-b-ethylene oxide)/poly(ethylene glycol) blend membranes  

作　　者：Shichao Feng Jizhong Ren Dan Zhao Hui Li Kaisheng Hua Xinxue Li Maicun Deng 

机构地区：[1]State Key Laboratory of Biochemical Engineering, Institute of Process Engineering, Chinese Academy of Sciences [2]National Laboratory for Clean Energy, Dalian Institute of Chemical Physics, Chinese Academy of Sciences

出　　处：《Journal of Energy Chemistry》2019年第1期39-45,共7页能源化学（英文版）

基　　金：Financial support from the National Science and Technology Planning Project (No. 2011BAC08B00);the National High Technology Research and Development Program of China (863 Program) (No.2012AA03A611)

摘　　要：Membranes from block copolymer poly(amide-12-b-ethylene oxide)(Pebax1074) and its blends with different molecular weight poly(ethylene glycol)(PEG)(200, 400, 600, 1500, 4600 and 8000) were prepared. The thermal properties and structures of Pebax1074/PEG blend membranes were characterized by DSC and SEM, and the gas permeation properties of CO_2 and N_2 were also investigated at different temperatures. For Pebax1074/PEG blend membranes with low molecular weight PEG(MW≤ 600), higher gas permeabilities than Pebax1074 were achieved. The permeability increased with the increase of PEG molecular weight. The addition of low molecular weight PEG resulted in decrease in activation energy of permeation. For Pebax1074/PEG blend membranes with high molecular weight PEG(MW≥ 1500), due to the melt of PEO phase crystals, the gas permeation properties of blend membranes were temperaturedependent, which could be divided into crystalline region, transition region and amorphous region according to two different transition temperatures. PEG molecular weight and operation temperature determined different gas permeation properties of Pebax1074/PEG blend membranes in three regions. The activation energies of permeation in crystalline region were larger than those in amorphous region.Membranes from block copolymer poly(amide-12-b-ethylene oxide)(Pebax1074) and its blends with different molecular weight poly(ethylene glycol)(PEG)(200, 400, 600, 1500, 4600 and 8000) were prepared. The thermal properties and structures of Pebax1074/PEG blend membranes were characterized by DSC and SEM, and the gas permeation properties of CO_2 and N_2 were also investigated at different temperatures. For Pebax1074/PEG blend membranes with low molecular weight PEG(MW≤ 600), higher gas permeabilities than Pebax1074 were achieved. The permeability increased with the increase of PEG molecular weight. The addition of low molecular weight PEG resulted in decrease in activation energy of permeation. For Pebax1074/PEG blend membranes with high molecular weight PEG(MW≥ 1500), due to the melt of PEO phase crystals, the gas permeation properties of blend membranes were temperaturedependent, which could be divided into crystalline region, transition region and amorphous region according to two different transition temperatures. PEG molecular weight and operation temperature determined different gas permeation properties of Pebax1074/PEG blend membranes in three regions. The activation energies of permeation in crystalline region were larger than those in amorphous region.

关 键 词：Poly(amide-12-b-ethylene oxide) Polyethylene glycol Blend membrane Carbon dioxide separation 

分 类 号：O4[理学—物理]