TiO_2对CaO-MgO-P_2O_5-SiO_2系玻璃晶化影响的研究  

Studies on the Crystallization Dynamics of Ca-P-Si Glass-Ceramic

作　　者：俞冰[1] 梁开明[1] 顾守仁[1] 

机构地区：[1]清华大学材料科学与工程系,北京100084

出　　处：《无机材料学报》2002年第3期470-474,共5页Journal of Inorganic Materials

摘　　要：ＣａＯ－ＭｇＯ－Ｐ２Ｏ５－ＳｉＯ２系微晶玻璃是一种新型医学生物材料,该材料不仅具有良好的生物相容性,还具有一定的力学性能．本文采用差热分析(ＤＴＡ)方法对以ＴｉＯ２作为晶核剂的该系生物微晶玻璃的析晶动力学参数进行了测定。所得数据经计算机拟合后,其结果表明:在一定范围内引入ＴｉＯ２(≤８．７ｗｔ%)能降低该系玻璃的析晶活化能Ｅ,有促进玻璃析晶的作用;当ＴｉＯ２含量达到８．７ｗｔ%时,Ｅ达到最小值;当ＴｉＯ２含量＞８．７ｗｔ%时,Ｅ值反而回升．晶化指数ｎ与该玻璃体系中加入ＴｉＯ２的变化规律与Ｅ值随ＴｉＯ２的变化规律是一致的．CaO-MgO-P2O5-SiO2 glass-ceramic is a new medicinal biologic material. It not only has good biocompatibility but also improves mechanical properties. The kinetic parameters of this glass-ceramic were calculated by differential thermal analysis (DTA) and the JMA equation. The results indicate that the content of TiO2 effects on the crystallization activation energy (E) and the crystal growth index (n). E increases with the increasing of TiO2 content. And E reaches a max value when TiO2 content is about 8.7%. When TiO2 content increases further (>8.7%), E decreases inversely. The rule of n vs TiO2 content is consistent with that of E vs TiO2 content.

关 键 词：TiO2 CaO-MgO-P2O5-SiO2系玻璃 晶化 生物微晶玻璃 析晶 差热分析 氧化钙 氧化镁 五氧化二磷 生物材料 二氧化钛 二氧化硅 

分 类 号：TQ171.7[化学工程—玻璃工业] R318.08[化学工程—硅酸盐工业]