YBCO超导薄膜中磁通宏观量子蠕动现象的研究  

MAGNETIC RELAXATION STUDY OF MACROSCOPIC QUANTUM CREEPING IN YBCO FILMS

作　　者：李春光[1] 罗胜[2] 张国华[2] 沈庆飞[1] 何豫生[1] 金铎[1] 熊光成[3] 连贵君[3] 尹道乐[3] 

机构地区：[1]中国科学院物理研究所,北京2711信箱100080 [2]北京科技大学应用科学学院,北京100083 [3]北京大学物理系,北京100871

出　　处：《低温物理学报》2002年第2期129-132,共4页Low Temperature Physical Letters

摘　　要：我们对低温下YBCO(1 2 3)超导薄膜样品中磁通的宏观量子蠕动效应进行了研究 .用SQUID磁强计测量了厚度分别为 2 .4nm、6.0nm、1 0 .8nm和 40 .0nm的YBCO超导超薄膜样品和厚为 2 0 0nm的YBCO薄膜样品的磁化弛豫性质 .通过对样品磁化弛豫性质的分析我们在YBCO超导超薄膜样品中观察到明显的磁通的宏观量子蠕动效应 .各样品发生量子蠕动效应的温度Tcr在 8～1 5K之间 ,大大高于以前人们在YBCO单晶样品中观察到的Magnetic relaxations of YBCO films with thickness ranging from 2.4nm to 200nm have been studied using a commercial SQUID. Magnetic relaxation measurements show strong quantum creeping effects at temperatures as high as 8.5～15K in ultra thin films (2.4～40nm), whereas in 200nm film it is dominated by thermal activation down to \{4.2K\}. The T\-\{cr\} of ultra thin films is much higher than that reported in YBCO thick films or single crystals by others.

关 键 词：YBCO 超导薄膜 磁通 宏观量子蠕动 高温超导体 超导电性 钇钡铜氧化物 磁通动力学 

分 类 号：O511.4[理学—低温物理]