纳米Al_2O_3和SiO_2对刚玉质耐火材料烧结与力学性能的影响  

Influences of nano-alumina and nano-silica on sintering and mechanical property of corundum refractories

作　　者：赵惠忠[1] 吴斌 汪厚植[1] 张文杰[1] 顾华志[1] 赵俊峰 魏晓芳 

机构地区：[1]武汉科技大学高温陶瓷与耐火材料湖北省重点实验室,武汉430081 [2]洛阳耐火材料集团有限责任公司

出　　处：《耐火材料》2002年第2期66-69,共4页Refractories

基　　金：武汉市科技计划项目 (2 0 0 110 0 70 88)。

摘　　要：在普通的刚玉质耐火材料中分别加入少量纳米Al2 O3和SiO2 ,研究了这两种纳米材料对经不同温度烧成后刚玉质耐火材料烧结与力学性能的影响。结果发现 :这两种纳米材料均能使刚玉制品的烧成温度降低 1 0 0～ 2 0 0℃ ,并在相同烧成条件下能使试样的常温抗折强度和耐压强度提高1～ 2倍。Adding a small quantity of nano alumina and nano silica in ordinary corundum refractories respectively,the influences of the two type nanomaterials on the sintering and mechanical property of corundum refractories after different temperatures treatment were studied.The results show that both the two type nanomaterials can decrease the calcining temperature within 100 to 200 ℃,and make the cold modulus of rupture and cold crushing strength of the samples increase within 100%～200% under the same calcination condition.

关 键 词：纳米粉 三氧化二铝 二氧化硅 刚玉质 耐火材料 烧结 力学性能 影响 

分 类 号：TQ175.712[化学工程—硅酸盐工业]