LiCr_(0.10)Mn_(l.90)O_4粒径分布对倍率放电性能的影响  

Effects of Licr_(0.10) Mn_(1.90)O_4 With Various Partile Sizes on Ratedischarge Properties

作　　者：李建刚[1] 唐致远[1] 王占良[1] 薛建军[1] 

机构地区：[1]天津大学化工学院,天津300072

出　　处：《天津大学学报（自然科学与工程技术版）》2002年第3期401-403,共3页Journal of Tianjin University：Science and Technology

基　　金：天津市自然科学基金资助项目 (990 346)

摘　　要：以不同粒径 L i Cr0 .1 0 Mnl.90 O4 为活性物制备电极 ,与对电极锂片装配成模拟电池后进行电化学性能研究 .结果表明 ,随着 L i Cr0 .1 0 Mn1 .90 O4 粒径的增大 ,锂离子传输困难与 Jahn-Teller畸变导致其倍率充放电性能逐渐下降 .兼顾到活性物的填充性能 ,选择粒径大约 10μm的活性物较为适宜 .The rate discharge properties of LiCr 0 10 Mn 1 90 O 4 with various particle sizes are determined The results indicate LiCr 0 10 Mn l 90 O 4 with a larger particle size exhibits poor rate discharge properties, which could be attributed to its slower lithium ion diffusion and more serious Jahn Teller distortion Considering the tap density and rate discharge properties, an average 10 μm size of LiCr 0 10 Mn 1 90 O 4 is found to be more suitable as cathode material for lithium ion batteries

关 键 词：粒径分布 倍率放电 尖晶石 电池 正极材料 

分 类 号：TM24[一般工业技术—材料科学与工程]