在役加氢反应器材料损伤分析  

Analysis of the damage to the material used in the hydrogenation reactor

作　　者：谈金祝[1] 黄卫民[2] 

机构地区：[1]南京工业大学机械与动力工程学院,江苏南京210009 [2]扬子石油化工股份有限公司芳烃厂,江苏南京210048

出　　处：《南京工业大学学报（自然科学版）》2002年第3期47-50,共4页Journal of Nanjing Tech University(Natural Science Edition)

摘　　要：基于随加氢反应器运行 5a的试验试块 ,研究了加氢反应器运行 5a后筒体材料 2 .2 5Cr 1Mo钢的损伤。进行了化学成分分析、拉伸和冲击试验、脱氢和脱脆试验以及断口形貌分析。结果表明 :反应器运行 5a后筒体母材及其焊缝金属的拉伸性能未发生明显变化 ,而冲击韧性明显降低 ,且焊缝金属损伤程度较母材严重。经分析 。Based on the test block which was removed after five years exposure to the process environment within a hydrogenation reactor, the damage to 2.25Cr 1Mo steel used in the hydrogenation reactor was studied. Chemical compositions examination, tensile and impact tests, de hydrogenation and de brittleness heat treatment, and fracture surface analysis were performed. Tensile test results show that the tensile properties of the material have not degraded after five years exposure to the environment. The results of impact tests show that the toughness of the material after five years exposure to the environment has degraded and the degree of the toughness degradation for weld metal is much more than that of base metal. The test results reveal that the toughness degradation is caused by the high temperature tempering during long term service.

关 键 词：材料损伤 加氢反应器 钢 高温回火 断口形貌 

分 类 号：TQ052[化学工程]