超细碳酸钙的制备与表征  

Preparation and Characterization of Ultrafine Calcium Carbonate

作　　者：申小清[1] 杜燕军[2] 许闽[3] 任海波 

机构地区：[1]郑州大学材料工程学院,河南郑州450052 [2]安阳师范学院学报编辑部,4550023 [3]河南中医学院中药系,河南郑州450003 [4]平顶山工业中专学校,467000

出　　处：《安阳师范学院学报》2002年第2期27-29,共3页Journal of Anyang Normal University

摘　　要：分别以硅酸钠和硫酸锌为晶型控制添加剂 ,通过石灰乳碳化工艺制备超细CaCO3 粉体。研究了添加剂用量对CaCO3 颗粒尺寸的影响 ,并用TEM ,XRD和TG -DTA对CaCO3 粉体进行了表征。结果表明 ,添加 0 .7% - 1.5 %硅酸钠和 0 .5 % - 1.2 %硫酸锌可分别制得颗粒尺寸为 4 0 - 5 0nm和 4 0 - 6 0nm的球形和立方形超细CaCO3Ultrafine CaCO 3 powders were prepared by the carbonation of lime milk using sodium silicate and Zinc sulfate as crystallizing additives respectively. The effect of the amount of additives on the particle size of CaCO 3 was studies and TEM, XRD, TG-DTA were employed to Characterize the CaCO 3 powders. The results show that the globular CaCO 3 with the size of 40-50nm,40-60nm can be obtained by adding 0.7%-1.5% of sodium silicate and 0.5%-1.2% of zinc sulfate respectively.

关 键 词：超细碳酸钙 CACO3 超细粉体 制备 表征 硅酸钠 硫酸锌 石灰乳 碳化工艺 

分 类 号：TQ132.32[化学工程—无机化工] TB383[一般工业技术—材料科学与工程]