Investigation on Quick Surface Metallization of Nano Titania Powder  

纳米二氧化钛表面快速金属化的研究(英文)

作　　者：徐丽娜[1] 周凯常[1] 刘春平[2] 欧丹林[2] 顾宁[1] 刘举正[2] 陈坤基[3] 

机构地区：[1]东南大学分子与生物分子电子学教育部重点实验室,南京210096 [2]东南大学化学化工系,南京210096 [3]南京大学固体微结构开放实验室,南京210008

出　　处：《Journal of Southeast University(English Edition)》2002年第1期92-94,共3页东南大学学报（英文版）

基　　金：theNationalNaturalScienceFoundationofChina (69890 2 2 0 );OpenProjectFoundationofLaboratoryofSolidStateMi crostructuresofNanjingUniversity.

摘　　要：Quick surface metallization of titania powder was carried out by electrolesschemical deposition of nickel. The fabricated product was characterized by XRD, SEM, FTIR andcross-section metallography. The analysis results show that titania particles are completely coatedby a thin nickel shell about 600 nm thick composed of nano-sized crystalline nickel particles.Mechanism of nickel chemical deposition on nano powder is proposed.采用镍的无电子化学沉积方法研究了纳米二氧化钛粉末表面的快速金属化 .所得产物经XRD、SEM、FTIR及剖面金相显微术进行了表征 .分析结果表明二氧化钛粒子完全被金属镍包覆 ,金属壳层 6 0 0nm厚 ,由镍的纳米晶粒组成 .由此提出了镍在纳米粉末上的化学沉积机理 .

关 键 词：electroless chemical deposition nickel methallization nano titania 

分 类 号：O647.11[理学—物理化学]