聚丙烯酸酯原位乳液聚合包覆SiO_2的研究  

Study on Acrylic Resin Encapsulated SiO_2 of In-suit Emulsion Polymerization

作　　者：童筱莉[1] 邬润德[1] 王锐兰[1] 

机构地区：[1]浙江工业大学化工学院,杭州310014

出　　处：《有机硅材料》2002年第4期1-4,共4页Silicone Material

基　　金：浙江省科技招标项目 ;计划编号 0 1110 16 9

摘　　要：用经甲基丙烯酰氧基丙基三乙氧基硅烷 (MAPS)处理过的纳米SiO2 作种子 ,进行聚丙烯酸酯(ACR)的原位乳液聚合 ,制成了MAPS -SiO2 /ACR复合物 ;探讨了种子乳液聚合的过程 ,分析了包覆机理 ,讨论了SiO2 的用量对聚合反应速率及残渣率的影响。结果表明 :在以纳米SiO2 为种子的ACR乳液聚合中 ,单体的转化率及聚合反应速率随SiO2 用量的增加而下降 ;当SiO2 的用量为 1 0 %时 ,复合物与聚氯乙烯共混后 ,其拉伸强度和冲击强度最高。s:SiO 2/ACR composite was synthesized by acrylic resin of in suit emulsion polymerization using nano SiO 2 particle as core treated with MAPS and acrylic resin as shell; then made ultimately. The process of in suit emulsion polymerization was approached, its encapsulation mechanics was analyzed, and the effect of SiO 2 amount on the reacting velocity and sediment percentage was discussed. It was indicated that in the process of ACR emulsion polymerization with nano SiO 2 particle as core, the more amount of SiO 2, the less rate of conversion and polymerization of the monomer. The composite material, which blended with 10 % SiO 2 encapsulated ACR and PVC resin, had excellent tensile strength and impact strength compared with blend of the pure ACR and PVC resin.

关 键 词：原位乳液聚合 包覆 研究 聚丙烯酸酯 甲基丙烯酰氧基丙基三乙氧基硅烷 纳米二氧化硅 聚氯乙烯 

分 类 号：TQ316.3[化学工程—高聚物工业]