添加Cu粉对Ni-Cr合金真空钎焊金刚石磨粒界面组织的影响  

Effect of Microstructure of Vacuum Brazing Diamond Abrasive with Ni-Cr Alloy Added Copper Powder

作　　者：赵彬[1] 贺亚勋 卢金斌[1] 赵鹏[1] 张理想[1] 

机构地区：[1]中原工学院,郑州450007

出　　处：《中原工学院学报》2014年第3期29-32,78,共5页Journal of Zhongyuan University of Technology

基　　金：新型钎焊材料国家重点实验室开放课题(SKLABFMT201003);河南省省院科技合作项目(122106000051)

摘　　要：为降低金刚石高温钎焊后的热损伤,采用添加5%、10%、15%(wt%)Cu粉的Ni-Cr-B-Si钎料对金刚石磨粒进行了真空钎焊试验,实现了金刚石与钢基体的高强度连接.采用SEM对金刚石与钎料界面及碳化物形貌进行了观察分析。结果表明:添加5%Cu的Ni-Cr-B-Si钎料在1 050℃时钎焊能够实现金刚石与钎料的高强度连接,不仅对金刚石润湿较好,也能在一定程度上减少金刚石的热损伤。In order to reduce the thermal damage ot diamond under high temperature aiter brazing, using Ni-Cr-B-Si alloy added 5%, 10%, 15% （wt%） copper powder brazing diamond in vacuum, a high- strength bonding between steel base and diamond is achieved. The interface between diamond and filler and car- bide formed on the diamond surface is analyzed by using SEM. Results show that a firm joint between steel base and diamond is obtained by using Ni-Cr-B-Si alloy added 5 - （wt%） copper powder brazing diamond in vacuum, and it is good to the wettability of the diamond, and can decrease the thermal damage of diamond to a certain extent.

关 键 词：真空钎焊 润湿性 热损伤 化学冶金结合 金刚石 

分 类 号：TG142[一般工业技术—材料科学与工程]