硫磺硫化体系组成对EPDM/CM共混卷材力学性能的影响  

Influence of Sulphur Vulcanizing System Composition on Mechanical Properties of EPDM/CM Blended Membrane

作　　者：孙剑 刘晓东 张冬冬 

机构地区：[1]潍坊宏源防水材料有限公司,山东潍坊262700

出　　处：《中国建筑防水》2014年第14期12-15,共4页China Building Waterproofing

摘　　要：通过调整硫化体系中硫磺(S)和硫化促进剂(TMTD)的用量,研究了EPDM/CM共混卷材的力学性能。结果表明,TMTD用量为1 phr(每百克橡胶或树脂中的含量)时,S用量为1.5 phr时EPDM/CM共混卷材的力学性能最佳;TMTD用量为1.5 phr时,S用量为1.25 phr时EPDM/CM共混卷材的力学性能最佳;后者综合性能优于前者。The article studies the mechanical properties of EPDM/CM blended membrane through adjusting the dosages of sulphur （S） and accelerator （TMTD） in the vulcanizing system. The results show that when the dosage of TMTD is 1 phr （the content of 100 g rubber or resin）, and the dosage of S is 1.5 phr, the mechanical properties of EPDM/CM membrane are the best; while the dosage of TMTD is 1.5 phr, and the dosage of S is 1.25 phr, the EPDM/CM membrane＇s mechanical properties are optimal. The comprehensive properties of the latter formulation is better.

关 键 词：三元乙丙橡胶 弹性体型氯化聚乙烯 硫磺 TMTD 力学性能 

分 类 号：TU573[建筑科学—建筑技术科学]