Structure and luminescent properties of luminous polypropylene fiber based on Sr_2MgSi_2O_7:Eu^(2+),Dy^(3+)  

作　　者：罗军 高强 张开砚 葛明桥 刘佳林 

机构地区：[1]Key Laboratory of Science and Technology of Eco-Textiles, Ministry of Education, Jiangnan University

出　　处：《Journal of Rare Earths》2014年第8期696-701,共6页稀土学报（英文版）

基　　金：supported by National Natural Science Foundation of China(21171074);Fundamental Research Funds for the Central Universities of China(JUSRP21003);the National Undergraduate Training Programs for Innovation(201310295046)

摘　　要：The luminous polypropylene fiber based on long afterglow luminescent material Sr2MgSi2O7：Eu^2＋,Dy^3＋was prepared by melt-spinning process. Micro-morphology, phase composition, crystal structure, spectral features and afterglow properties of the lu-minescent fiber were tested and analyzed. The results indicated that the fiber had independent superposition phase features of both Sr2MgSi2O7：Eu2＋,Dy3＋and polypropylene. The range of its excitation wavelength was located between 250-450 nm;therefore, the luminescent fiber could be excited by ultraviolet or visible light. It could emit blue light of 460 nm wavelength after excitation, which was caused by the 5d-4f transition of Eu^2＋ions within the host lattice. The initial luminescent intensity was more than 0.8 cd/m^2, and afterglow life lasted 7 h. The afterglow decay was composed of rapid-decaying and slow-decaying processes, and the decay charac-teristics depended on the depth and concentration of trap level in the Sr2MgSi2O7：Eu^2＋,Dy^3＋.The luminous polypropylene fiber based on long afterglow luminescent material Sr2MgSi2O7：Eu^2＋,Dy^3＋was prepared by melt-spinning process. Micro-morphology, phase composition, crystal structure, spectral features and afterglow properties of the lu-minescent fiber were tested and analyzed. The results indicated that the fiber had independent superposition phase features of both Sr2MgSi2O7：Eu2＋,Dy3＋and polypropylene. The range of its excitation wavelength was located between 250-450 nm;therefore, the luminescent fiber could be excited by ultraviolet or visible light. It could emit blue light of 460 nm wavelength after excitation, which was caused by the 5d-4f transition of Eu^2＋ions within the host lattice. The initial luminescent intensity was more than 0.8 cd/m^2, and afterglow life lasted 7 h. The afterglow decay was composed of rapid-decaying and slow-decaying processes, and the decay charac-teristics depended on the depth and concentration of trap level in the Sr2MgSi2O7：Eu^2＋,Dy^3＋.

关 键 词：luminescent fiber rare-earth luminescent materials SR2MGSI2O7 long afterglow 

分 类 号：TQ422[化学工程]