Observation of etch pits in Fe-36wt%Ni Invar alloy  

作　　者：Dong-zhu Lu Min-jie Wu 

机构地区：[1]Division of Surface Engineering of Materials,Institute of Metal Research,Chinese Academy of Sciences

出　　处：《International Journal of Minerals,Metallurgy and Materials》2014年第7期682-686,共5页矿物冶金与材料学报（英文版）

摘　　要：To indirectly investigate the dislocation behavior of Fe-36wt%Ni Invar alloy by the etch pit method, polished Invar specimens were etched by a solution containing 4 g copper sulfate, 20 mL hydrochloric acid, and 20 mL deionized water for 2 min. Etch pits in the etched surfaces were observed. All the etch pits in one specific grain exhibited similar shapes, which are closely related to the grain orienta-tions. These etch pits were characterized as dislocation etch pits. It was observed that etch pits arranged along grain boundaries, gathered at grain tips and strip-like etch pit clusters passed through a number of grains in the pure Invar specimens. After the addition of a small amount of alloying elements, the identification of a single dislocation etch pit is challenging compared with the pure Invar alloy. Thus, the observation of etch pits facilitates the investigation on the dislocation behavior of the pure Invar alloy. In addition, alloying elements may affect the densities and sizes of etch pits.To indirectly investigate the dislocation behavior of Fe-36wt%Ni Invar alloy by the etch pit method, polished Invar specimens were etched by a solution containing 4 g copper sulfate, 20 mL hydrochloric acid, and 20 mL deionized water for 2 min. Etch pits in the etched surfaces were observed. All the etch pits in one specific grain exhibited similar shapes, which are closely related to the grain orienta-tions. These etch pits were characterized as dislocation etch pits. It was observed that etch pits arranged along grain boundaries, gathered at grain tips and strip-like etch pit clusters passed through a number of grains in the pure Invar specimens. After the addition of a small amount of alloying elements, the identification of a single dislocation etch pit is challenging compared with the pure Invar alloy. Thus, the observation of etch pits facilitates the investigation on the dislocation behavior of the pure Invar alloy. In addition, alloying elements may affect the densities and sizes of etch pits.

关 键 词：Invar alloy dislocations etch pit technique alloying elements 

分 类 号：TG131[一般工业技术—材料科学与工程]