高温热处理毛竹材诱发变色机理研究  被引量:10

The Induced Discoloration Mechanism of High Temperature Heat-treated Bamboo

在线阅读下载全文

作  者:沈钰程[1] 王云芳[1] 汤颖[1] 李延军[1] 

机构地区:[1]浙江农林大学工程学院,浙江临安311300

出  处:《竹子研究汇刊》2013年第4期42-45,共4页Journal of Bamboo Research

基  金:浙江省科技厅项目(2012R10023-05);浙江农林大学研究生科研创新基金项目(3122013240223);浙江农林大学大学生创新训练计划项目(201204034)

摘  要:采用4年生中部毛竹,对其进行160℃、180℃、200℃热处理2 h。定性观察高温热处理后毛竹颜色的直观变化,借助化学成分分析和红外光谱分析方法,研究高温热处理竹材的诱发变色机理。结果表明:高温热处理后,竹材木质素含量上升,增加了20.89%。木质素中发色基团增多,助色基团也发生了变化,从而导致了热处理竹材的诱发变色。特征官能团甲氧基峰值发生蓝移,波长减小,使得竹片外观颜色变深。The induced discoloration mechanism of high temperature heat-treated bamboo was studied using the methods of chemical component analysis and FTIR. The middle sections of the 4-year-old bamboo poles were heat-treaded for 2 h under 160℃ , 180℃ ,200℃ respectively in dry oven. The results showed that the content of lignin increased by 20.89% after heat treatment. Number of ehromophoric group raised and auxoehrome group had changed. The peak of methoxy group, which is a characteristic functional group of lignin, appeared blue shift. The wavelength of visible light decreased. As a result, bamboo chips turned darker.

关 键 词:采用4年生中部毛竹 对其进行160℃、180℃、200℃热处理2h 定性观察高温热处理后毛竹颜色的直观变化 借助化学成分分析和红外光谱分析方法 研究高温热处理竹材的诱发变色机理 结果表明 高温热处理后 竹材木质素含量上升 增加了20 89% 木质素中发色基团增多 助色基团也发生了变化 从而导致了热处理竹材的诱发变色 特征官能团甲氧基峰值发生蓝移 波长减小 使得竹片外观颜色变深 高温热处理 毛竹 变色机理 木质素 FTIR 

分 类 号:S795[农业科学—林木遗传育种]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象