富氧燃烧技术在1100t/d生产线应用试验  

Application of oxygen-enrichment technology on 1 100t/d cement production line

作　　者：朱文尚[1,2] 颜碧兰[1] 齐砚勇[1,2,3] 王俊杰[1] 汪澜[1] 宋军华[1] 

机构地区：[1]中国建筑材料科学研究总院绿色建筑材料国家重点实验室,北京100024 [2]武汉理工大学材料科学与工程学院,湖北武汉430070 [3]西南科技大学材料科学与工程学院,四川绵阳621010

出　　处：《水泥》2014年第9期6-8,共3页Cement

基　　金："十二五"国家科技支撑计划(2011BAE29B01)资助项目

摘　　要：针对章丘华明水泥有限公司1100t/d生产线进行富氧燃烧试验。结果表明,水泥回转窑通入富氧并调整窑系统工艺参数之后,熟料产量提高约20%,窑筒体温度升高,预热器C1出口和烟室NOx浓度提高,热耗下降约7.6%,预热器出口废气显热下降约8.1%。The oxygen-enriched combustion pilot test was applied on 1 100t/d Zhangqiu Huaming cement limited company kiln. The results showed that after the oxygen-enriched air added into the rotary kiln, and process parameters of kiln system adjusted, the clinker production increased around 20%, the kiln shell surface temperature increased, the NOx concentration of preheater outlet and smoke chamber at kiln end increased, the heat consumption decreased about 7.6%, and the gas sensible heat of preheater exit dropped nearly 8.1%.

关 键 词：富氧燃烧 产量 筒体温度 气体成分 