异戊橡胶的序列结构及其与结晶性能的关系  

Relationship between sequence structure of polyisoprene and its crystallization performance

作　　者：李曙光[1] 谭金玫 贺经纬[1,3] 王秀娟 吴丝竹[1,3] 

机构地区：[1]北京化工大学有机无机复合材料国家重点实验室,北京100029 [2]中国石化北京北化院 燕山分院,北京102500 [3]北京化工大学北京市新型高分子材料制备与成型加工重点实验室,北京100029

出　　处：《合成橡胶工业》2014年第5期368-372,共5页China Synthetic Rubber Industry

基　　金：国家自然科学基金资助项目(50973007);中国石油化工股份有限公司资助项目(H 2011395)

摘　　要：研究了几种不同牌号的异戊橡胶(IR)的序列结构及其与结晶性能之间的关系。结果表明,不同牌号的IR具有不同的序列结构,而序列结构的不同导致IR的结晶性能存在差异,其中高顺式-1,4-结构的IR具有良好的结晶性能,而反式-1,4-结构和3,4-结构的存在会降低IR分子链的规整度,不利于结晶。The relationship between the sequence structure of different brands of polyisoprene （IR） and their crystallization performance was studied.The results showed that there was different sequence structures among different brands of IR,which led to different crystallization performances.IR with high content of cis-1,4-unit had good crystallization performance,while the existence of trans-1,4 and 3,4-units reduced the regularity of IR molecular chain,which was unfavorable to crystallization.

关 键 词：异戊橡胶 序列结构 冷结晶 诱导结晶 应力弛豫 

分 类 号：TQ333.3[化学工程—橡胶工业]