Al_2O_(3p)和Gr_p对Al基复合材料磨损性能的影响  

Aluminum-based composite materials strengthened by Al_2O_3 and Gr binary powders and its wear properties

作　　者：宋月波[1] 李永靖[2] 龙律位 杨建林[2] 

机构地区：[1]辽宁工程技术大学思想政治理论教研部,辽宁阜新123000 [2]辽宁工程技术大学材料学院,辽宁阜新123000

出　　处：《辽宁工程技术大学学报（自然科学版）》2014年第7期943-946,共4页Journal of Liaoning Technical University (Natural Science)

基　　金：辽宁工程技术大学科研启动基金资助项目(11-417)

摘　　要：为研究Al2O3和Gr双相颗粒对Al基复合材料耐磨性的影响,采用粉末冶金法制备了不同Al2O3和Gr质量分数的Al基复合材料,利用X射线衍射仪、布氏硬度计、ML-10摩擦磨损机、扫描电镜等手段对样品的物相组成、硬度、磨损性、表面显微形貌进行表征.结果表明:随Al2O3的增加,样品的硬度逐渐增大.试样的耐磨性随Al2O3质量分数的增加先增大后减小,Al2O3的质量分数为9%的样品具有良好耐磨性.在润滑油下,试样的磨损机制主要为磨粒磨损.Aluminum-based composite materials with different AlO23 and Gr powder quantities were synthesized by powder metallurgy. Phase, Brinell hardness, wear properties and surface micro-morphology were tested by X-ray diffractometer, Brinell hardness tester, ML-10 type wear testing machine and scanning electron microscope, respectively. The result shows that with increasing of AlO23 content, the hardness increases. The wear resistance increases and then decreases as the AlO23 content increases. The sample with 9% of AlO23 powders has the best wear resistance. The main wear mechanism of sample under oil lubrication is abrasive wear.

关 键 词：粉末冶金 铝基复合材料 AL2O3 磨损 硬度 

分 类 号：TG135[一般工业技术—材料科学与工程]