Energy transfer relation of a novel Ce^(3+)/Pr^(3+)/Eu^(3+) co-doped Sr_(2.975-x)La_xAlO_(4+x)F_(1-x) solid solution phosphor  

作　　者：王延泽 马健 孙亮 李蕊 王达健 

机构地区：[1]Institute of Materials Physics, School of Materials Science and Engineering, Tianjin University of Technology

出　　处：《Chinese Physics B》2014年第10期546-550,共5页中国物理B（英文版）

基　　金：Project supported by the National Natural Science Foundation of China(Grant Nos.21076161 and 50872091)

摘　　要：The photoluminescence properties and energy transfer of a new Ce3＋/pr3＋/Eu3＋ co-doped solid-solution composi- tion of Sr2.975-xLaxAlO4＋xF1-x （LSAF） phosphor are investigated. Upon doping Pr3＋ into lattices of LSAF：Ce host, a shoulder emission peak is observed at about 620 nm, owing to the transition of 1D2 →3H4. Addition of Eu3＋ to LSAF：Ce3＋, Pr3＋ phosphor results in a sharp emission peaked at 675 nm for the 5D0 →TF3 transition and an increase of the intensity of red emission for Pr3＋ with increasing Eu3＋ concentration. The pathways of energy transfer among Ce3＋, Pr3＋, and Eu3＋ are proposed to be responsible for color addition of a red component to the primary yellow emission, enabling a potential adjustable color for blue excitable warm white.The photoluminescence properties and energy transfer of a new Ce3＋/pr3＋/Eu3＋ co-doped solid-solution composi- tion of Sr2.975-xLaxAlO4＋xF1-x （LSAF） phosphor are investigated. Upon doping Pr3＋ into lattices of LSAF：Ce host, a shoulder emission peak is observed at about 620 nm, owing to the transition of 1D2 →3H4. Addition of Eu3＋ to LSAF：Ce3＋, Pr3＋ phosphor results in a sharp emission peaked at 675 nm for the 5D0 →TF3 transition and an increase of the intensity of red emission for Pr3＋ with increasing Eu3＋ concentration. The pathways of energy transfer among Ce3＋, Pr3＋, and Eu3＋ are proposed to be responsible for color addition of a red component to the primary yellow emission, enabling a potential adjustable color for blue excitable warm white.

关 键 词：energy transfer solid solution red emission PHOSPHOR 