Synthesis and Crystal Structure of 1D Cd-amine Coordination Polymer and Its Luminescent Properties  

作　　者：XU Mengying LIU Zhigang FAN Ruiqing GAO Song CHEN Shuo YANG Yulin 

机构地区：[1]Department of Chemistry, Harbin Institute of Technology, Harbin 150001, P. R. China

出　　处：《Chemical Research in Chinese Universities》2014年第5期720-725,共6页高等学校化学研究（英文版）

基　　金：Supported by the National Natural Science Foundation of China（Nos.21371040, 21171044）, the National Key Basic Re- search Program of China（No.2013 CB632900）, the Fundamental Research Funds for the Central Universities of China（No.201409） and the Program for Innovation Research of Science in Harbin Institute of Technology, China（Nos.A201416, B201414）.

摘　　要：A novel one dimension（1D） cadmium coordination polymer {[Cd（mpda）3]·2（NO3）}n（1） was synthesized via refluxing a mixture of tetradentate Schiff base ligand N,N＇-bis（2-pyridinylethylidene）phenylene-1,3-diamine（L） and Cd（NO3）2 in acetonitrile, whose structure was characterized by means of single crystal X-ray diffraction, FTIR spectroscopy, elemental analysis and proton nuclear magnetic resonance（1H NMR）. Center metal Cd（II） ion is six-coordinated by six nitrogen atoms from six different m-phenylenediamine（mpda）, giving rise to a [CdN6] octahe- dral coordination environment. The two adjacent cadmium centers are linked by three mpda molecules leading to the construction of 1D chain structure. The crystal structure is stabilized by N-H…O hydrogen bonds to form three-dimension supramolecule. Compound 1 exhibits intense yellow luminescence in solid state at 298 K（λem=554 nm）, which shows a blue shift at 77 K（ca. 147 nm）. Additionally, fluorescence characteristics of compound 1 were investigated in different solvents（polarity： DMSO〉CH3CN〉CH3OH〉CHC13〉toluene） at 298 and 77 K. The results show that the emission peak of compound 1 in solvent exhibits a slight bathochromic shift. However, the emission peaks of compound 1 in CH3OH and CHC13 are red shift compared with that in CH3CN. It is revealed that the lumi- nescence behavior of compound 1 depends on not only the polarity of solvent but also the hydrogen bonding proper- ties between solvent and solute. In addition, the emission peak of compound 1 in solution shows a red shift obviously at 77 K than that at 298 K（ca. 144-159 nm）, with the fluorescence lifetime increased at 77 K. The lifetime in DMSO at 77 K（r=12.470μs） was the longest one. The quantum yield of compoud 1 increases with increasing the polarity of solvent within a range of 1.8%-8.3 %.A novel one dimension（1D） cadmium coordination polymer {[Cd（mpda）3]·2（NO3）}n（1） was synthesized via refluxing a mixture of tetradentate Schiff base ligand N,N＇-bis（2-pyridinylethylidene）phenylene-1,3-diamine（L） and Cd（NO3）2 in acetonitrile, whose structure was characterized by means of single crystal X-ray diffraction, FTIR spectroscopy, elemental analysis and proton nuclear magnetic resonance（1H NMR）. Center metal Cd（II） ion is six-coordinated by six nitrogen atoms from six different m-phenylenediamine（mpda）, giving rise to a [CdN6] octahe- dral coordination environment. The two adjacent cadmium centers are linked by three mpda molecules leading to the construction of 1D chain structure. The crystal structure is stabilized by N-H…O hydrogen bonds to form three-dimension supramolecule. Compound 1 exhibits intense yellow luminescence in solid state at 298 K（λem=554 nm）, which shows a blue shift at 77 K（ca. 147 nm）. Additionally, fluorescence characteristics of compound 1 were investigated in different solvents（polarity： DMSO〉CH3CN〉CH3OH〉CHC13〉toluene） at 298 and 77 K. The results show that the emission peak of compound 1 in solvent exhibits a slight bathochromic shift. However, the emission peaks of compound 1 in CH3OH and CHC13 are red shift compared with that in CH3CN. It is revealed that the lumi- nescence behavior of compound 1 depends on not only the polarity of solvent but also the hydrogen bonding proper- ties between solvent and solute. In addition, the emission peak of compound 1 in solution shows a red shift obviously at 77 K than that at 298 K（ca. 144-159 nm）, with the fluorescence lifetime increased at 77 K. The lifetime in DMSO at 77 K（r=12.470μs） was the longest one. The quantum yield of compoud 1 increases with increasing the polarity of solvent within a range of 1.8%-8.3 %.

关 键 词：Schiffbase Cd（II）-amine compound LUMINESCENCE Crystal structure 

分 类 号：O614.242[理学—无机化学] O614.121[理学—化学]