Preparation of Polypropylene Multifunctional White Masterbatch with Antistatic and Anti-aging Properties

作　　者：刘芝芳[1] 单德才[1] 吴红枚[1] 王孟[1] 陈国庆 

机构地区：[1]南华大学化学化工学院,湖南衡阳421001 [2]中山市铁鹰塑胶有限公司,广东中山528463

出　　处：《南华大学学报（自然科学版）》2014年第3期92-94,共3页Journal of University of South China：Science and Technology

基　　金：中山市产学研基金资助项目(2013C2FC0027);湖南省教育厅基金资助项目(13C798)

摘　　要：本文通过单因素实验确定制备抗静电防老化的聚丙烯(PP)多功能白色母粒的优化配方.结果表明:载体树脂为60 kg,色素为12 kg,抗静电剂为10 kg,抗氧剂为10 kg,分散剂为6 kg,增容剂为2 kg是制备100 kg的多功能白色母粒的最佳配比.用该功能母粒制备的聚丙烯板材的表面电阻系数为0.6×109,氙灯老化500 h后色牢度为5级.In this paper,the optimum ratio of preparing the multifunctional white masterbatch with antistatic and anti-aging properties was ascertained by single factor experiments. The results show that the best ratio for preparing 100 kg multifunctional white masterbatch： carrier resin is 60 kg,colorant is 12 kg,antistatic agent is 10 kg,anti-oxygen is 10 kg,dispersant is 6 kg,compatibilizer is 2 kg. The surface resistance of polypropylene plates made from the multifunctional masterbatch is 0. 6 × 10^9,and the color fastness is level five after xenon-arc lamp 500 h aging.

关 键 词：聚丙烯 多功能 母粒 抗静电 防老化 

分 类 号：TQ340.4[化学工程—化纤工业]