A novel multifunction material with both electrorheological performance and luminescence property  

作　　者：陈明星 商艳丽 贾云玲 李俊然 

机构地区：[1]College of Chemistry and Molecular Engineering, Peking University [2]College of Chemistry and Environmental Science, Hebei University

出　　处：《Journal of Rare Earths》2014年第11期1022-1026,共5页稀土学报（英文版）

基　　金：Project supported by National Natural Science Foundation of China(10704041,90922033,21071008);the National Basic Research Program of China(2013CB933401,2010CB934601)

摘　　要：A multifunctional material with both electrorheological（ER） performance and luminescence property was synthesized by a simple coprecipitation. The tetrabutyl titanate, as well as the Tb（NO3）3·6H2O and sulphosalicylic acid（C7H6O6S·2H2O, SSA） were chosen as starting materials. The composition, ER performance and luminescence property of the material were studied. The results showed that a novel material（TiTbSSA） with both ER performance and luminescence property was obtained. The relative shear stress τr（τr=τE/τ0, τE and τ0 were the shear stresses of the suspension with and without an applied electric field） of the suspension（30 wt.%） of the material in silicone oil reached 32.7 at a shear rate of 12.5 s–1 and an electric field strength of 4 kV/mm（DC electric field）. The material containing the rare earth（RE=Tb） complex exhibited fine luminescence performance and higher ER activity. Therefore, it is a novel multifunction material which would have wide application prospect.A multifunctional material with both electrorheological（ER） performance and luminescence property was synthesized by a simple coprecipitation. The tetrabutyl titanate, as well as the Tb（NO3）3·6H2O and sulphosalicylic acid（C7H6O6S·2H2O, SSA） were chosen as starting materials. The composition, ER performance and luminescence property of the material were studied. The results showed that a novel material（TiTbSSA） with both ER performance and luminescence property was obtained. The relative shear stress τr（τr=τE/τ0, τE and τ0 were the shear stresses of the suspension with and without an applied electric field） of the suspension（30 wt.%） of the material in silicone oil reached 32.7 at a shear rate of 12.5 s–1 and an electric field strength of 4 kV/mm（DC electric field）. The material containing the rare earth（RE=Tb） complex exhibited fine luminescence performance and higher ER activity. Therefore, it is a novel multifunction material which would have wide application prospect.

关 键 词：multifunctional material electrorheological performance luminescence property rare earth complex 

分 类 号：TB34[一般工业技术—材料科学与工程]