Shear Fracture of Advanced High Strength Steels  

作　　者：Sheng HUANG Yi-xi ZHAO Chun-feng HE 

机构地区：[1]State Key Laboratory of Mechanical System and Vibration,Shanghai Jiao Tong University [2]Shanghai Key Laboratory of Digital Manufacture for Thin-walled Structures,Shanghai Jiao Tong University

出　　处：《Journal of Iron and Steel Research International》2014年第10期938-944,共7页

基　　金：Item Sponsored by National Natural Science Foundation of China(51075267);International Cooperation Program in Science and Technology of MOST of China(2010DFA72760)

摘　　要：Failure experiments were carried out through a stretch-bending test system for advanced high strength steels, i.e. dual-phase （DP） steels and martensitic steels （MS）. The die radius in this system was designed from 1 to 15 mm to investigate the failure mode under different geometries. Two failure modes were observed during the ex- periments. As a result, critical relative radii （the ratio of inner bending radius R to sheet thickness t） for DP590 and DP780 steels were obtained. The stretch-bending tests of DP980 display some trends unlike DP590 and DP780 steels, and curve of DP980 in different thicknesses does not coincide well. High blank holder force exhibits more possibility of shear fracture tendency than low blank holder force. The unique character of high strength martensitic steel （1500MS） is that no shear fracture is found especially over small bending radius （R =2 mm） under the same experi- mental conditions. Microstructure analysis indicates that there are obviously elongated grains on shear fracture sur- face. It shows smaller diameter and shallower depth of the dimples than the necking failure.Failure experiments were carried out through a stretch-bending test system for advanced high strength steels, i.e. dual-phase （DP） steels and martensitic steels （MS）. The die radius in this system was designed from 1 to 15 mm to investigate the failure mode under different geometries. Two failure modes were observed during the ex- periments. As a result, critical relative radii （the ratio of inner bending radius R to sheet thickness t） for DP590 and DP780 steels were obtained. The stretch-bending tests of DP980 display some trends unlike DP590 and DP780 steels, and curve of DP980 in different thicknesses does not coincide well. High blank holder force exhibits more possibility of shear fracture tendency than low blank holder force. The unique character of high strength martensitic steel （1500MS） is that no shear fracture is found especially over small bending radius （R =2 mm） under the same experi- mental conditions. Microstructure analysis indicates that there are obviously elongated grains on shear fracture sur- face. It shows smaller diameter and shallower depth of the dimples than the necking failure.

关 键 词：advanced high strength steel shear fracture critical R/t blank holder force MICROSTRUCTURE 

分 类 号：TG142.1[一般工业技术—材料科学与工程]