A new low-cost method of reclaiming mixed foundry waste sand based on wet-thermal composite reclamation  

作　　者：Fan Zitian Liu Fuchu Long Wei Li Guona 

机构地区：[1]State Key Laboratory of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology

出　　处：《China Foundry》2014年第5期402-407,共6页中国铸造（英文版）

基　　金：supported by the National Natural Science Foundation (Grant numbers:50575085,51075163 and 51375187)

摘　　要：A lot of mixed clay-resin waste sand from large-scale iron foundries is discharged every day; so mixed waste sand reclamation in low cost and high quality has a great realistic significance. In the study to investigate the possibility of reusing two types of waste foundry sands, resin bonded sand and clay bonded sand which came from a Chinese casting factory, a new low-cost reclamation method of the mixed foundry waste sand based on the wet-thermal composite reclamation was proposed. The waste resin bonded sand was first reclaimed by a thermal method and the waste clay bonded sand was reclaimed by a wet method. Then, hot thermal reclaimed sand and the dehydrated wet reclaimed sand were mixed in certain proportions so that the hot thermal reclaimed sand dried the wet reclaimed sand leaving some water. The thermal reclamation efficiency of the waste resin bonded sand was researched at different heat levels. The optimized wet reclamation process of the waste clay bonded sand was achieved by investigating the effects of wet reclamation times, sand-water ratio and pH value on the reclaimed sand characteristics. The composite reclamation cost also was calculated. The research results showed that the properties of the mixed reclaimed sand can satisfy the application requirements of foundries; in which the temperature of the thermal reclamation waste resin bonded sand needs to be about 800 oC, the number of cycles of wet reclamation waste clay bonded sand should reach four to five, the optimal sand-water ratio of wet reclamation is around 1:1.5, and the pH value should be adjusted by adding acid. The mass ratio of hot thermal reclaimed sand to dehydrated wet reclaimed sand is about 1:2.5, and the composite reclaimed sand cost is around 100 yuan RMB per ton.A lot of mixed clay-resin waste sand from large-scale iron foundries is discharged every day; so mixed waste sand reclamation in low cost and high quality has a great realistic significance. In the study to investigate the possibility of reusing two types of waste foundry sands, resin bonded sand and clay bonded sand which came from a Chinese casting factory, a new low-cost reclamation method of the mixed foundry waste sand based on the wet-thermal composite reclamation was proposed. The waste resin bonded sand was first reclaimed by a thermal method and the waste clay bonded sand was reclaimed by a wet method. Then, hot thermal reclaimed sand and the dehydrated wet reclaimed sand were mixed in certain proportions so that the hot thermal reclaimed sand dried the wet reclaimed sand leaving some water. The thermal reclamation efficiency of the waste resin bonded sand was researched at different heat levels. The optimized wet reclamation process of the waste clay bonded sand was achieved by investigating the effects of wet reclamation times, sand-water ratio and pH value on the reclaimed sand characteristics. The composite reclamation cost also was calculated. The research results showed that the properties of the mixed reclaimed sand can satisfy the application requirements of foundries; in which the temperature of the thermal reclamation waste resin bonded sand needs to be about 800 oC, the number of cycles of wet reclamation waste clay bonded sand should reach four to five, the optimal sand-water ratio of wet reclamation is around 1：1.5, and the pH value should be adjusted by adding acid. The mass ratio of hot thermal reclaimed sand to dehydrated wet reclaimed sand is about 1：2.5, and the composite reclaimed sand cost is around 100 yuan RMB per ton.

关 键 词：sand casting process mixed waste sand HIGH-QUALITY LOW-COST sand reclamation 

分 类 号：TG221[金属学及工艺—铸造]