催化分解二茂铁制备碳纳米片及其结构表征  

Synthesis and characterization of carbon nanosheets by catalytic pyrolysis of ferrocene

作　　者：闫博[1] 张龙梅[1] 张俊豪[1] 

机构地区：[1]江苏科技大学环境与化学工程学院,江苏镇江212018

出　　处：《江苏科技大学学报（自然科学版）》2014年第4期337-341,共5页Journal of Jiangsu University of Science and Technology:Natural Science Edition

基　　金：江苏省高校自然科学基金资助项目(13KJB430012);江苏省自然科学基金资助项目(BK20141293)

摘　　要：以二茂铁为催化剂和碳源，硫粉为辅助剂，采用催化分解技术，在500℃时制备碳纳米片，成炭率高达95％左右．结构测试结果表明：酸处理后的主要产物为非晶碳纳米片，其厚度约为40 nm．氮气吸附脱附结果表明：合成的碳纳米片为介孔材料的特征吸附脱附等温线，比表面积为41.1 m2/g，孔径主要集中在3.5～5 nm．A catalytic pyrolysis approach was developed to synthesize carbon nanosheets with a yield of above 95%at 500℃ by using ferrocene as catalyst and carbon source and S powder as additive .The results of struc-tural test show that the main products after acid treatment are amorphous carbon nanosheets with a thickness of 40 nm.The results of N 2 adsorption-desorption isotherm indicate the BET surface area of carbon nanosheets is 41.1 m2/g,and the pore-size distribution centered from 3.5 to 5 nm.

关 键 词：催化分解 纳米片 拉曼谱 透射电镜 N2 吸附脱附等温线 

分 类 号：O613.71[理学—无机化学] TQ127.11[理学—化学]